Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Cast, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.490 - 1.80 g/cc
0.0177 - 0.0649 lb/in³
Average value: 1.14 g/cc Grade Count:26
Water Absorption 0.100 - 10.0 %
0.100 - 10.0 %
Average value: 0.911 % Grade Count:22
Viscosity 10.0 - 180000 cP
10.0 - 180000 cP
Average value: 20300 cP Grade Count:52
46.0 - 1800 cP

@Temperature 52.0 - 100 °C
46.0 - 1800 cP

@Temperature 126 - 212 °F
Average value: 717 cP Grade Count:9
Linear Mold Shrinkage 0.00100 cm/cm
0.00100 in/in
Average value: 0.00100 cm/cm Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell M 85.0 - 121
85.0 - 121
Average value: 100 Grade Count:6
Hardness, Shore D 6.00 - 90.0
6.00 - 90.0
Average value: 62.9 Grade Count:44
>= 70.0

@Temperature 120 - 120 °C
>= 70.0

@Temperature 248 - 248 °F
Average value: 72.4 Grade Count:6
60.0 - 85.0

@Temperature 100 - 100 °C
60.0 - 85.0

@Temperature 212 - 212 °F
Average value: 72.4 Grade Count:7
60.0 - 85.0

@Time 10800 - 10800 sec
60.0 - 85.0

@Time 3.00 - 3.00 hour
Average value: 72.4 Grade Count:7
Tensile Strength, Ultimate 7.58 - 96.5 MPa
1100 - 14000 psi
Average value: 48.2 MPa Grade Count:56
Elongation at Break 0.700 - 400 %
0.700 - 400 %
Average value: 25.4 % Grade Count:46
Modulus of Elasticity 0.827 - 10.0 GPa
120 - 1450 ksi
Average value: 3.74 GPa Grade Count:17
Flexural Yield Strength 13.8 - 131 MPa
2000 - 19000 psi
Average value: 75.1 MPa Grade Count:28
Flexural Modulus 0.0138 - 3.79 GPa
2.00 - 550 ksi
Average value: 2.59 GPa Grade Count:10
Compressive Yield Strength 13.8 - 279 MPa
2000 - 40500 psi
Average value: 109 MPa Grade Count:32
Shear Strength 7.58 - 17.2 MPa
1100 - 2500 psi
Average value: 13.2 MPa Grade Count:3
Adhesive Bond Strength 6.89 - 19.3 MPa
1000 - 2800 psi
Average value: 13.1 MPa Grade Count:6
Izod Impact, Notched 0.246 - 1.13 J/cm
0.460 - 2.12 ft-lb/in
Average value: 0.430 J/cm Grade Count:9
Thermal Properties Metric English Comments
CTE, linear 12.0 - 90.0 µm/m-°C
6.67 - 50.0 µin/in-°F
Average value: 44.3 µm/m-°C Grade Count:14
Thermal Conductivity 0.167 - 0.795 W/m-K
1.16 - 5.52 BTU-in/hr-ft²-°F
Average value: 0.480 W/m-K Grade Count:20
Maximum Service Temperature, Air 20.0 - 300 °C
68.0 - 572 °F
Average value: 121 °C Grade Count:59
Minimum Service Temperature, Air -269 - -46.1 °C
-452 - -51.0 °F
Average value: -94.4 °C Grade Count:12
Optical Properties Metric English Comments
Transmission, Visible 90.0 %
90.0 %
Average value: 90.0 % Grade Count:11
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 - 9.00e+16 ohm-cm
1.00e+12 - 9.00e+16 ohm-cm
Average value: 6.80e+15 ohm-cm Grade Count:35
1.00e+8 - 1.00e+15 ohm-cm

@Temperature 66.0 - 130 °C
1.00e+8 - 1.00e+15 ohm-cm

@Temperature 151 - 266 °F
Average value: 7.80e+13 ohm-cm Grade Count:7
Surface Resistance 7.38e+11 - 7.85e+15 ohm
7.38e+11 - 7.85e+15 ohm
Average value: 3.41e+15 ohm Grade Count:6
Dielectric Constant 2.79 - 4.50
2.79 - 4.50
Average value: 3.52 Grade Count:30
2.66 - 5.60

@Temperature 100 - 150 °C
2.66 - 5.60

@Temperature 212 - 302 °F
Average value: 4.06 Grade Count:12
2.66 - 5.60

@Frequency 60.0 - 1000 Hz
2.66 - 5.60

@Frequency 60.0 - 1000 Hz
Average value: 4.06 Grade Count:12
Dielectric Strength 11.8 - 21.7 kV/mm
300 - 550 kV/in
Average value: 16.3 kV/mm Grade Count:24
Dissipation Factor 0.00500 - 0.0550
0.00500 - 0.0550
Average value: 0.0219 Grade Count:19
0.00700 - 0.142

@Temperature 100 - 150 °C
0.00700 - 0.142

@Temperature 212 - 302 °F
Average value: 0.0580 Grade Count:11
0.00700 - 0.142

@Frequency 60.0 - 60.0 Hz
0.00700 - 0.142

@Frequency 60.0 - 60.0 Hz
Average value: 0.0580 Grade Count:11
Arc Resistance 150 sec
150 sec
Average value: 150 sec Grade Count:6
Processing Properties Metric English Comments
Cure Time 1.00 - 30200 min
0.0167 - 504 hour
Average value: 3380 min Grade Count:18
20.0 - 3600 min

@Temperature 50.0 - 204 °C
0.333 - 60.0 hour

@Temperature 122 - 400 °F
Average value: 198 min Grade Count:40
Pot Life 2.50 - 4320 min
2.50 - 4320 min
Average value: 373 min Grade Count:65
16.0 - 420 min

@Temperature 60.0 - 100 °C
16.0 - 420 min

@Temperature 140 - 212 °F
Average value: 93.8 min Grade Count:20