Aclo Accutech Polypropylene Copolymer CP0437W20L Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437W20L Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 58 | 58 | ASTM D785 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ASTM D638 |
| Elongation at Break | 18 % | 18 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 1.300 GPa | 188.5 ksi | ASTM D638 |
| Flexural Strength | 19.0 MPa | 2760 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 1.71 J/cm | 3.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F |
Users viewing this material also viewed the following:
- Quantum Composites Lytex® 9063 63% Glass Fiber Epoxy SMC
- Inhance Fluoro-Seal INHANCE® HD-1035 HDPE
- Borealis SuperCOPO™ LH4201R Polyethylene Insulation Compound, Crosslinkable
- Total PPH 4060 Polypropylene, Homopolymer
- CP-Polymer-Technik Wellamid® 6000 GV 25 HWUVCP 25% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Conditioned
- Daikin POLYFLON D-2E PTFE Dispersion
- Chosun Refractories L12S Magnesia Carbon Bricks for Ladle Slag Line
- Aclo Accucomp Polycarbonate POL051L Medium Viscosity
- Akzo Nobel Trigonox® A-80 Polymerization Initiator
Copyright © lookpolymers.com All Rights Reserved