Lubrizol Isoplast® 2530 Engineering Thermoplastic Polyurethane Resin for Medical Applications
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Isoplast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Isoplast® 2530 Engineering Thermoplastic Polyurethane Resin for Medical Applications.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.13 % | 0.13 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 55 | 55 | ASTM D785 |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ASTM D638 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | ASTM D638 |
| Elongation at Break | 160 % | 160 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 1.90 GPa | 276 ksi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Unnotched | 0.850 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.59 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| 0.950 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
1.78 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 75.0 J @Temperature -29.0 °C |
55.3 ft-lb @Temperature -20.2 °F |
ASTM D3763 |
| 80.0 J @Temperature 23.0 °C |
59.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | Unannealed; ASTM D648 |
| 93.0 °C | 199 °F | Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Unannealed; ASTM D648 |
| 89.0 °C | 192 °F | Annealed; ASTM D648 | |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 10 % | 10 % | ASTM D1925 |
| Transmission, Visible | 93 % | 93 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 243 °C | 430 - 469 °F | |
| Mold Temperature | 66.0 - 82.0 °C | 151 - 180 °F | |
| Drying Temperature | 85.0 - 91.0 °C | 185 - 196 °F |
Users viewing this material also viewed the following:
- Nye Lubricants 377AL (RL) Synthetic Oil
- Rogers Corporation RO4835 Hydrocarbon Ceramic Laminate, Improved Oxidation Resistance
- ICO Polymers ICORENEâ„¢ 195-1336 LMDPE Rotational Molding Resin
- Karina 600-DA-48/1-C-IS Black PVC Compound
- Gromax BTE35-DN00N1 Nylon 6 (Conditioned)
- Teknor Apex APEX® 3610-85 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics LNP STAT-KON 9X04323 PPE+PA66 (Asia Pacific)
- Eurostar Starflam M10009A PP, Flame Retardant, Injection Molding
- Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Dry, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved