Lubrizol Estane® 2103-70A Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTANE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Estane® 2103-70A Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Formerly PellethaneFeature: High MVTRAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | -0.00300 - 0.0080 cm/cm | -0.00300 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 8.70 kg, Temperature 224 °C |
11 g/10 min @Load 19.2 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | ASTM D2240 |
| Tensile Strength, Ultimate | 24.7 MPa | 3580 psi | ASTM D412 |
| Elongation at Break | 730 % | 730 % | ASTM D412 |
| 50% Modulus | 0.00210 GPa | 0.305 ksi | ASTM D412 |
| 100% Modulus | 0.00300 GPa | 0.435 ksi | ASTM D412 |
| 300% Modulus | 0.00520 GPa | 0.754 ksi | ASTM D412 |
| Tear Strength | 66.5 kN/m | 379 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 3.0 | 3.0 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 25 % @Temperature 25.0 °C, Time 79200 sec |
25 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395, Method B |
| 75 % @Temperature 70.0 °C, Time 79200 sec |
75 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395, Method B | |
| Tensile Set | 50 % | 50 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 175 µm/m-°C @Temperature 20.0 °C |
97.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Vicat Softening Point | 75.0 °C | 167 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Glass Transition Temp, Tg | -69.0 °C | -92.2 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 204 °C | 370 - 399 °F | Extrusion |
| 193 - 210 °C | 379 - 410 °F | Molding | |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 82.0 - 93.0 °C | 180 - 199 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- RheTech Products GC20P255-00 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Natural
- Nilit FRIANYL B63 SG-GV 2515 Nylon 6 for injection molding, 25% mineral filled and 15% glass fiber reinforced
- Kazanorgsintez 107-276 Low Density Polyethylene Composition with Improved Processibility
- Fainplast Compounds RKI 0223 Rigid PVC, Antishock Injection Molding Lead Free
- Solvay Specialty Polymers Aquivion® E87-12S Tetrafluoroethylene + SFVE (TFE+SFVE)
- SABIC Innovative Plastics LNP Thermocomp GX05053 PSU (Europe-Africa-Middle East)
- A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66
- DSM Stanyl® 46HF4130 (DAM) Nylon 46 30% Glass Reinforced, Heat Stabilized, High Flow (North America)
- Overview of materials for Nylon 66, 20% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved