Lubrizol ESTANE® GP92AE Ester Based Thermoplastic Polyurethane

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTANE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol ESTANE® GP92AE Ester Based Thermoplastic Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Type: Estane® GP 92AE is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided by Lubrizol.

Physical Properties	Metric	English	Comments
Specific Gravity	1.23 g/cc	1.23 g/cc	ISO 2781
Maximum Moisture Content	0.050	0.050
Melt Flow	15 - 40 g/10 min @Load 8.70 kg, Temperature 215 °C	15 - 40 g/10 min @Load 19.2 lb, Temperature 419 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	92	92	ISO 868
Tensile Strength, Ultimate	43.0 MPa	6240 psi	ISO 37
Elongation at Break	650 %	650 %	ISO 37
Tensile Modulus	0.0280 GPa	4.06 ksi	ISO 527
50% Modulus	0.00750 GPa	1.09 ksi	ISO 37
100% Modulus	0.00900 GPa	1.31 ksi	ISO 37
300% Modulus	0.0150 GPa	2.18 ksi	ISO 37
Rebound	40 %	40 %	ISO 4662
Tear Strength	85.0 kN/m	485 pli	with incision; ISO 34B
	121 kN/m	690 pli	without incision; ISO 34B
Abrasion	35	35	mm<sup>3</sup>; ISO 4649
Compression Set	23 %	23 %	70 hrs./22°C; ISO 815
	33 %	33 %	24 hrs./70°C; ISO 815

Thermal Properties	Metric	English	Comments
Vicat Softening Point	115 °C	239 °F	A50; ISO 306

Processing Properties	Metric	English	Comments
Feed Temperature	40.0 °C	104 °F	Injection
Nozzle Temperature	190 - 200 °C	374 - 392 °F	Injection
Zone 1	185 - 195 °C	365 - 383 °F	Injection
Zone 2	190 - 200 °C	374 - 392 °F	Injection
Zone 3	195 - 205 °C	383 - 401 °F	Injection
Zone 4	195 - 205 °C	383 - 401 °F	Injection
Drying Temperature	100 °C	212 °F
Dry Time	2.00 - 3.00 hour	2.00 - 3.00 hour
Dew Point	-30.0 °C	-22.0 °F