BLUESTAR LXS 112 PPE-PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Unreinforced |
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BLUESTAR LXS 112 PPE-PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: PV Industrial partsFire RatedInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 300 °C |
40 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | type I; ASTM D638 |
| Elongation at Break | 25 % | 25 % | type I; ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-326 (HS-HAF)
- Abatron AboCast 8101-3/AboCure 8101-3 Epoxy (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP RB00A PA 66 (Europe-Africa-Middle East)
- Teknor Apex Telcar® TL-150 BLK288 Thermoplastic Elastomer
- Polyplastics FR-PET® B3030FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose
- Tipco Tipcolite® THD 311 Phenolic Compound, Wood Flour, having Medium Flow & High Strength
- Zotefoams Evazote® VA35 Ethylene Vinyl Acetate Copolymer Foam
- Aclo Accutech Polypropylene Copolymer CP0436G40CL Glass Reinforced
- Aclo Accutech Polypropylene Homopolymer HP0336M30CL Mica Reinforced Coupled
- ATI Allegheny Ludlum Grade 17 Titanium (UNS R52252)
Copyright © lookpolymers.com All Rights Reserved