Lanxess Pocan® B 3215 901510 PBT, 10% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® B 3215 901510 PBT, 10% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 10% glass fibers, injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0012 cm/cm | 0.0012 in/in | ISO 294-4, 2577 |
| Melt Flow | 33 g/10 min @Load 2.16 kg, Temperature 260 °C |
33 g/10 min @Load 4.76 lb, Temperature 500 °F |
Calculated from MVR using melt density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-1/-2 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 |
| Tensile Modulus | 4.90 GPa | 711 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Vicat Softening Point | 205 °C | 401 °F | 50°C/h 50N; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ A70 white Polyamide 66 (Nylon 66)
- Lehmann & Voss LUVOCOM® 1/CF/10/GF/20/BK Polyamide 66, with carbon fiber and glass fiber, heat stabilized
- Special Metals DURANICKEL® 301 (UNS N03301) Annealed Wire
- Ensinger Tecapeek® XP-98 Medical Compression Molded PEEK Compound, 30% Carbon Fiber
- Covestro Makroblend® DP UT3905 Polycarbonate + PBT, Impact Grade
- 3M P592 Metal Primer
- Plastcom SLOVAMID 6 GB 20 PA6 reinforced with 20% glass beads
- SABIC Innovative Plastics Lexan® HFD4412 PC (Europe-Africa-Middle East)
- Loctite® Ultra Grey® 5699 Flange Sealant
Copyright © lookpolymers.com All Rights Reserved