Lehmann & Voss LUVOCOM® 80-8162 Polyacetal-copolymer, lubricant modified
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-8162 Polyacetal-copolymer, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, glide mating with low sliding friction.High dimensionally stable precision parts.Bearings, sleeves, high precision gear wheels, control disks, rollers, coil formers.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.018 - 0.030 cm/cm | 0.018 - 0.030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 48.0 MPa | 6960 psi | |
| Elongation at Yield | 20 % | 20 % | |
| 25 % | 25 % | flexural | |
| Modulus of Elasticity | 2.30 GPa | 334 ksi | |
| Flexural Strength | 70.0 MPa | 10200 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (white) |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 5012 C Natural Polypropylene
- Rogers Corporation RO4003C Glass-Reinforced Hydrocarbon and Ceramic Laminate with Thin Film Resistor Foil
- Omni Plastics OmniTech™ CPP XE72-A BK17 ESD Polypropylene Conductive
- 3M Dyneon™ Fluorel™ FC-2181 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C
- Master Bond EP33CLV Epoxy Resists Chemicals and High Temperatures
- Beijing Chemical Industry KAIFA® 301-G15 PBT Resin
- HP Alloys Alloy 718, 5% Cold Worked, Aged
- Schott BG28 Band Pass Filter
Copyright © lookpolymers.com All Rights Reserved