SABIC Innovative Plastics Lexan® ML7686 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® ML7686 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent Polycarbonate in limited colors. Excellent processability, super high flow. UL rated V-2 at 1.5mm.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.350 %
0.350 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.28 %
0.28 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 23 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 23 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
45 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 45 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Melt Index of Compound 43 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 43 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
50 mm/min; ISO 527
Tensile Strength, Yield 75.0 MPa
10900 psi
50 mm/min; ISO 527
Elongation at Break 60 %
60 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.80 GPa
406 ksi
1 mm/min; ISO 527
Flexural Yield Strength 110 MPa
16000 psi
2 mm/min; ISO 178
Flexural Modulus 2.70 GPa
392 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.400 J/cm
0.749 ft-lb/in
ASTM D256
0.450 J/cm

@Temperature -30.0 °C
 0.843 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*3; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) >= 100 kJ/m²
>= 47.6 ft-lb/in²
80*10*3; ISO 180/1U
>= 100 kJ/m²

@Temperature -30.0 °C
 >= 47.6 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched >= 10.0 J/cm²
>= 47.6 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eU
>= 10.0 J/cm²

@Temperature -30.0 °C
 >= 47.6 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 80.0 J

@Temperature 23.0 °C
 59.0 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 36.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
72.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 40.0 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 67.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
74.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 41.1 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 106 °C
223 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
103 °C

@Thickness 3.20 mm
 217 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 112 °C
234 °F
Rate B/50; ISO 306
113 °C
235 °F
Rate B/50; ASTM D1525
115 °C
239 °F
Rate B/120; ISO 306
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
 UL 94
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified