Akro-Plastic Akromid® A3 (2414) PA 6.6 Conditioned

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	Akro-Plastic
Trade Name	Akromid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Akro-Plastic Akromid® A3 (2414) PA 6.6 Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatures as well as easy processing. AKROMID® A is an engineering plastic compound that allows a broad range of possible applications. On the basis of these standard types, we are able to develop individual compounds for special application needs.Information from Akro-Plastic

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	ISO 1183
Water Absorption	2.9 - 3.1 % @Temperature 70.0 °C	2.9 - 3.1 % @Temperature 158 °F	62% r.h., Humidity; ISO 62
Water Absorption at Saturation	8.0 - 9.0 % @Time 82800 sec	8.0 - 9.0 % @Time 23.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.019 cm/cm	0.019 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.023 cm/cm	0.023 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	50.0 MPa	7250 psi	5 [mm/min], Test Speed 50 [mm/min]; ISO 527-1/2
Elongation at Break	>= 50 %	>= 50 %	50 [mm/min]; ISO 527-1/2
Elongation at Yield	20 %	20 %	50 [mm/min]; ISO 527-2
Tensile Modulus	1.10 GPa	160 ksi	1[mm/min]; ISO 527-1/2
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.30 J/cm² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	262 °C	504 °F	ISO 11357-1/3

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093