Lehmann & Voss LUVOCOM® 1301-8291 PPS, linear, with aramid reinforcement

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Aramid Fiber Filled
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOM® 1301-8291 PPS, linear, with aramid reinforcement.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low warpage.dynamic stressInformation provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.38 g/cc	1.38 g/cc	ISO 1183
Water Absorption	<= 0.20 %	<= 0.20 %	23°C/24h
Linear Mold Shrinkage	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in

Mechanical Properties	Metric	English	Comments
Tensile Stress	80.0 MPa	11600 psi
Elongation at Yield	2.0 %	2.0 %
	2.6 %	2.6 %	flexural
Modulus of Elasticity	6.00 GPa	870 ksi
Flexural Strength	110 MPa	16000 psi
Flexural Modulus	5.00 GPa	725 ksi
Charpy Impact Unnotched	1.20 J/cm²	5.71 ft-lb/in²	edgewise; ISO 179 1eU

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	220 °C	428 °F
	240 °C	464 °F	short term

Electrical Properties	Metric	English	Comments
Surface Resistance	>= 1.00e+12 ohm	>= 1.00e+12 ohm
Insulation Resistance	>= 1.00e+12 ohm	>= 1.00e+12 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	330 °C	626 °F	mass temp
Nozzle Temperature	320 - 340 °C	608 - 644 °F
Zone 1	300 - 320 °C	572 - 608 °F
Zone 2	310 - 330 °C	590 - 626 °F
Zone 3	320 - 340 °C	608 - 644 °F
Mold Temperature	150 - 180 °C	302 - 356 °F
Drying Temperature	50.0 - 90.0 °C @Time >=14400 sec	122 - 194 °F @Time >=4.00 hour
	100 - 140 °C @Time 7200 - 14400 sec	212 - 284 °F @Time 2.00 - 4.00 hour	Dehumidifying dryer

Descriptive Properties	Value	Comments
Color	black