SABIC Innovative Plastics LNP Thermocomp MF006ASJ PP

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Thermocomp MF006ASJ PP.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP THERMOCOMP* MF006ASJ is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized, Healthcare.This data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/inÂ³	ASTM D 792
Linear Mold Shrinkage, Flow	0.0030 cm/cm @Time 86400 sec	0.0030 in/in @Time 24.0 hour	ASTM D 955
Linear Mold Shrinkage, Transverse	0.011 cm/cm @Time 86400 sec	0.011 in/in @Time 24.0 hour	ASTM D 955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	73.0 MPa	10600 psi	ASTM D 638
Elongation at Break	2.2 %	2.2 %	ASTM D 638
Flexural Strength	113 MPa	16400 psi	ASTM D 790
Flexural Modulus	6.20 GPa	899 ksi	ASTM D 790
Izod Impact, Notched	0.690 J/cm @Temperature 23.0 Â°C	1.29 ft-lb/in @Temperature 73.4 Â°F	ASTM D 256
Izod Impact, Unnotched	3.20 J/cm @Temperature 23.0 Â°C	5.99 ft-lb/in @Temperature 73.4 Â°F	ASTM D 4812

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	147 Â°C @Thickness 3.20 mm	297 Â°F @Thickness 0.126 in	unannealed; ASTM D 648