- Lehmann & Voss LUVOCOM® 1105-7327 PEEK, with glass fiber
Lehmann & Voss LUVOCOM® 1105-7327 PEEK, with glass fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7327 PEEK, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.82 g/cc | 1.82 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | |
| Melt Flow | 12.74 g/10 min @Load 5.00 kg, Temperature 380 °C |
12.74 g/10 min @Load 11.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 160 MPa | 23200 psi | |
| Elongation at Yield | 1.3 % | 1.3 % | |
| 2.2 % | 2.2 % | flexural | |
| Modulus of Elasticity | 19.0 GPa | 2760 ksi | |
| Flexural Strength | 250 MPa | 36300 psi | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color |
Users viewing this material also viewed the following:
- Polykemi AB POLYasa 2410F High Flow ASA
- Oxford Polymers PBT 30GF PBT, 30% Glass Fiber Reinforced
- H.C. Starck Amperit® 526.074 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17
- SABIC Innovative Plastics Valox® 745 PBT (Asia Pacific)
- DSM Stanyl® TE263F6 (COND) Nylon 46 30% Glass Reinforced, Heat Stabilized, Impact Modified (North America)
- Bohler-Uddeholm AISI D2 Cold Work Tool Steel
- BASF Lupranate® T80 Toluene Diisocyanate
- Ametek AM 388™ Alloy (UNS C72650) TB00 Solution HT
- Beijing Ranger Chem PBT 403 M-G10 HF Halogen Free Flame Retarding FR PBT
- 3M Scotch-Weld™ 2290 Epoxy Adhesive/Coating
Copyright © lookpolymers.com All Rights Reserved