Lord Adhesives Fusor® 310 A/B Epoxy Adhesive
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | Lord Adhesives |
| Trade Name | Fusor® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Fusor® 310 A/B Epoxy Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lord® 310 adhesive is a modified, thixotropic, two-part epoxy adhesive which bonds well to many types of prepared metals, prepared rubber, urethane, and plastics. Originally formulated for primerless adhesion to SMC, Lord 310 adhesive is used to bond disk drives, down-hole oil field equipment, automotive body panels, and spoilers, vibration dampening mounts and much more.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 - 1.32 g/cc | 0.0434 - 0.0477 lb/in³ | 310B Hardener |
| 1.40 - 1.54 g/cc | 0.0506 - 0.0556 lb/in³ | 310A Resin | |
| Solids Content | 100 % | 100 % | 310A Resin |
| 100 % | 100 % | 310B Hardener | |
| 100 % | 100 % | Mixed | |
| Water Absorption | 0.36 % @Time 86400 sec |
0.36 % @Time 24.0 hour |
ASTM D570-81 |
| Brookfield Viscosity | 230000 - 690000 cP @Temperature 25.0 °C |
230000 - 690000 cP @Temperature 77.0 °F |
310B Hardener; HBF, Helipath @ 5rpm |
| 400000 - 820000 cP @Temperature 25.0 °C |
400000 - 820000 cP @Temperature 77.0 °F |
310A Resin; HBF, Helipath @ 5rpm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | Lord TM 23B |
| Tensile Strength at Break | 32.1 MPa | 4650 psi | ASTM D882-83A (mod) |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D882-83A (mod) |
| Modulus of Elasticity | 1.69 GPa | 245 ksi | ASTM D882-83A (mod) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 327 µm/m-°C | 182 µin/in-°F | below Tg; ASTM D882-83A (mod) |
| 340 µm/m-°C | 189 µin/in-°F | above Tg; Lord Internal Method (by DMA) | |
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ASTM E1640-99 (by DMA) |
| Flash Point | >= 93.0 °C | >= 199 °F | 310A Resin; Closed Cup |
| >= 93.0 °C | >= 199 °F | 310B Hardener; Closed Cup | |
| >= 93.0 °C | >= 199 °F | Mixed; Closed Cup | |
| Shrinkage | 0.17 % | 0.17 % | 72 hours RT cure |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 1440 min @Temperature >=18.0 °C |
24.0 hour @Temperature >=64.4 °F |
|
| Pot Life | 30 - 60 min @Temperature 24.0 °C |
30 - 60 min @Temperature 75.2 °F |
54g mass |
| Shelf Life | 12.0 Month @Temperature 25.0 °C |
12.0 Month @Temperature 77.0 °F |
310A Resin |
| 12.0 Month @Temperature 25.0 °C |
12.0 Month @Temperature 77.0 °F |
310B Hardener |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Gray | 310B Hardener |
| Gray | Mixed | |
| Off-White | 310A Resin | |
| Consistency | Paste | 310A Resin |
| Paste | 310B Hardener | |
| Paste | Mixed | |
| Mix Ratio | 1.15:1 | by weight |
| 1:1 | by volume |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3960 TPE, PP Overmold or Standalone use
- Park Electrochemical Nelco® N4000-13 High-Speed Multifunctional Epoxy Laminate and Prepreg
- Techmer ES HiFill FR® ABS FR
- SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Europe-Africa-Middle East)
- Universal Wire Works 17-22ASVM (AMS 6458) Low Alloy Steel Welding Wire
- ExxonMobil PPU0180F Polypropylene Homopolymer
- Dow Latex XZ 92219.00 Experimental Latex
- Arlon 55869R028 0.0295" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Nextel™ BP-18 Woven Tape 312 (3.8 cm)
- Advanced Polymer Alloys Alcryn® 3065 NC Melt Processable Rubber
Copyright © lookpolymers.com All Rights Reserved