- Lehmann & Voss LUVOCOM® 1-7789/EG Polyamide 66, with carbon fiber, lubricant modified, heat stabilized
Lehmann & Voss LUVOCOM® 1-7789/EG Polyamide 66, with carbon fiber, lubricant modified, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-7789/EG Polyamide 66, with carbon fiber, lubricant modified, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Antistatic.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 170 MPa | 24700 psi | |
| Elongation at Yield | 3.5 % | 3.5 % | |
| 4.5 % | 4.5 % | flexural | |
| Modulus of Elasticity | 9.00 GPa | 1310 ksi | |
| Flexural Strength | 245 MPa | 35500 psi | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black-grey |
Users viewing this material also viewed the following:
- Nyco NYAD® 5000 Wollastonite
- Ineos Nova Zyntar® F7080 Developmental Flame Retardant Polystyrene (discontinued **)
- Kinlead PG13 Bag Grade BOPP Plain Film (thickness: 30 µm)
- LG Chemical LUPOL EI5002 PP
- Styron EMERGEâ„¢ 7550 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)
- CLAL-MSX NICLAL 1300 0 Annealed Copper Alloy, Free Cutting Nickel-Silver
- CMW® ELKONITE 40SB tungsten, silver
- Azoty Tarnow™ Alphalon™ E 36 LN Nylon 6
- Arlon 99202R008 0.008" (0.203 mm) Cured Silicone Rubber with PTFE Coated Fiberglass Carrier
- DuPont Performance Polymers Zytel® HTN FR52G30BL NC010 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved