- Lehmann & Voss LUVOCOM® 1-7395 Polyamide 66, with carbon fiber, aramid reinforcement and PTFE, heat stabilized
Lehmann & Voss LUVOCOM® 1-7395 Polyamide 66, with carbon fiber, aramid reinforcement and PTFE, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-7395 Polyamide 66, with carbon fiber, aramid reinforcement and PTFE, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved wear behaviour, low warpage.Emergency running property, for highest tribologic needs.Reduced moment of inertia compared with metal parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 155 MPa | 22500 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| 4.0 % | 4.0 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 220 MPa | 31900 psi | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| 150 °C | 302 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Nylene® CX3451 Translucent Nylon Copolymer
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR Tricresyl Phosphate
- Shin-Etsu Silicones KE-931U Silicone Elastomer
- Formosa Plastics Formolene® HB5502F Blow Molding HDPE
- Trelleborg Emerson & Cuming Eccobond® 83C Two-Component Silver Filled Electrically Conductive Epoxy Adhesive
- Entec Hypro™ PPH-GF30 Natural Homopolymer Polypropylene, 30% Glass Reinforced
- Arkema Group Rilsan® Powder T NAT BHV COS Nylon 11, Cosmetic Grade
- Ineos Nova 1220 High Heat Crystal Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved