SABIC Innovative Plastics LNP THERMOCOMP DF006ER PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF006ER PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF006ER is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| 1.425 g/cc | 0.05148 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0011 cm/cm @Time 86400 sec |
0.0011 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0048 cm/cm @Time 86400 sec |
0.0048 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 106 MPa | 15400 psi | ISO 527 |
| 132 MPa | 19100 psi | ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 |
| 2.7 % | 2.7 % | ASTM D638 | |
| Tensile Modulus | 7.50 GPa | 1090 ksi | 1 mm/min; ISO 527 |
| 9.51 GPa | 1380 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 196 MPa | 28400 psi | ISO 178 |
| 205 MPa | 29700 psi | ASTM D790 | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| 8.75 GPa | 1270 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.65 J/cm | 16.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CP - 1000 IG High Impact Acrylic Resin
- Polykemi AB SCANAMID 66 A33^E F30 Nylon 66, Glass Fiber Reinforced, Modified
- Premix Premi-Glas® 1201-10 Polyester SMC (discontinued **)
- GBC Grade 90 Alumina
- KEP Kepital® F40 Standard Grade/Low Viscosity Acetal Homopolymer
- SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific)
- Techmer ES HiFill® PES GF30 30% Glass Filled
- Teknor Apex Uniprene® UN-7100-40D Thermoplastic Vulcanizate
- Bulk Molding Compounds BMC SLC 2000 Glass Reinforced Polyester
Copyright © lookpolymers.com All Rights Reserved