- Asahi Kasei Thermylene® P6-30FG-0602 30% Glass Fiber Reinforced, UV Stabilized
Asahi Kasei Thermylene® P6-30FG-0602 30% Glass Fiber Reinforced, UV Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P6-30FG-0602 30% Glass Fiber Reinforced, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
| Flexural Modulus | 5.38 GPa | 780 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm | 1.60 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.07 J/cm | 9.50 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 675A(IF) Synthetic Oil
- IDI Composites W-102 Thermoset Polyester, Molding
- Shakespeare WN-38 diameter 0.4 mm Nylon 6 Monofilament
- A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66
- Eastman Tenite Butyrate 550E4861316 Clear, Trsp Cellulose Acetate Butyrate
- Diamond Polymers ABS 6501 Injection Molding Grade, Extra High Impact
- CMW® 28 Copper Alloy
- 3M 9828 Double Coated Tapes with Adhesive 340
Copyright © lookpolymers.com All Rights Reserved