Lanxess Pocan® ECO T 3220 000000 PBT + PET, 20% Glass Fiber

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® ECO T 3220 000000 PBT + PET, 20% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT + PET, 20% glass fibers, injection molding, improved surface finish, contains 28% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.47 g/cc
1.47 g/cc
ISO 1183
Bulk Density 0.800 g/cc
0.0289 lb/in³
ISO 60
Moisture Absorption at Equilibrium 0.20 %
0.20 %
50% RH; ISO 62
Water Absorption at Saturation 0.40 %
0.40 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0040 cm/cm
0.0040 in/in
60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.010 cm/cm
0.010 in/in
60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
ISO 527-1, -2; 5 mm/min
Elongation at Break 3.2 %
3.2 %
ISO 527-1, -2; 5 mm/min
Tensile Modulus 7.50 GPa
1090 ksi
ISO 527-1, -2; 1 mm/min
Flexural Strength 195 MPa

@Strain 3.50 %
 28300 psi

@Strain 3.50 %
 2 mm/min; ISO 178-A
Flexural Modulus 7.50 GPa
1090 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
35.0 kJ/m²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 225 - 250 °C
437 - 482 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75-1, -2
Vicat Softening Point 210 °C

@Load 5.10 kg
 410 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
270 °C
518 °F
for test specimens; ISO 294
Mold Temperature 80.0 - 100 °C
176 - 212 °F
90.0 °C
194 °F
for test specimens; ISO 294
Drying Temperature 120 °C
248 °F
Dry Time 4 - 8 hour
4 - 8 hour
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 7792-1-PBT+PET, GHMR, 09-070, GF20