DuPont Performance Polymers Rynite® 540SUV BK544 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Rynite® 540SUV BK544 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
40% Glass Reinforced UV Stabilized Polyethylene Terephthalate Developed for Extrusion and Injection Molding Rynite 540SUV BK544 is a 40% glass fiber reinforced UV stabilized modified polyethylene terephthalate resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.64 g/cc
0.0592 lb/in³
ISO 1183
Water Absorption 0.60 %
<br>@Thickness 2.00 mm
 0.60 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %
<br>@Thickness 2.00 mm
 0.150 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 162 MPa
23500 psi
ISO 527-1/-2
Tensile Stress 2.05 MPa
<br>@Strain 0.0600 %,<br> Temperature 90.0 °C
 297 psi
<br>@Strain 0.0600 %,<br> Temperature 194 °F
 ISO 11403-1 -2
2.79 MPa
<br>@Strain 0.0400 %,<br> Temperature 40.0 °C
 405 psi
<br>@Strain 0.0400 %,<br> Temperature 104 °F
 ISO 11403-1 -2
2.89 MPa
<br>@Strain 0.0400 %,<br> Temperature 23.0 °C
 419 psi
<br>@Strain 0.0400 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
3.01 MPa
<br>@Strain 0.0700 %,<br> Temperature 150 °C
 437 psi
<br>@Strain 0.0700 %,<br> Temperature 302 °F
 ISO 11403-1 -2
3.13 MPa
<br>@Strain 0.0400 %,<br> Temperature 0.000 °C
 454 psi
<br>@Strain 0.0400 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
3.85 MPa
<br>@Strain 0.0400 %,<br> Temperature -20.0 °C
 558 psi
<br>@Strain 0.0400 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
4.10 MPa
<br>@Strain 0.0400 %,<br> Temperature -40.0 °C
 595 psi
<br>@Strain 0.0400 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
9.40 MPa
<br>@Strain 0.260 %,<br> Temperature 150 °C
 1360 psi
<br>@Strain 0.260 %,<br> Temperature 302 °F
 ISO 11403-1 -2
13.67 MPa
<br>@Strain 0.200 %,<br> Temperature 90.0 °C
 1983 psi
<br>@Strain 0.200 %,<br> Temperature 194 °F
 ISO 11403-1 -2
14.93 MPa
<br>@Strain 0.140 %,<br> Temperature 40.0 °C
 2165 psi
<br>@Strain 0.140 %,<br> Temperature 104 °F
 ISO 11403-1 -2
15.13 MPa
<br>@Strain 0.130 %,<br> Temperature 23.0 °C
 2194 psi
<br>@Strain 0.130 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
15.43 MPa
<br>@Strain 0.130 %,<br> Temperature 0.000 °C
 2238 psi
<br>@Strain 0.130 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
17.77 MPa
<br>@Strain 0.130 %,<br> Temperature -40.0 °C
 2577 psi
<br>@Strain 0.130 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
21.47 MPa
<br>@Strain 0.170 %,<br> Temperature -20.0 °C
 3114 psi
<br>@Strain 0.170 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
32.08 MPa
<br>@Strain 0.210 %,<br> Temperature -40.0 °C
 4653 psi
<br>@Strain 0.210 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
32.32 MPa
<br>@Strain 0.270 %,<br> Temperature 40.0 °C
 4688 psi
<br>@Strain 0.270 %,<br> Temperature 104 °F
 ISO 11403-1 -2
37.1 MPa
<br>@Strain 1.99 %,<br> Temperature 150 °C
 5380 psi
<br>@Strain 1.99 %,<br> Temperature 302 °F
 ISO 11403-1 -2
37.99 MPa
<br>@Strain 0.300 %,<br> Temperature 0.000 °C
 5510 psi
<br>@Strain 0.300 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
39.84 MPa
<br>@Strain 0.290 %,<br> Temperature -20.0 °C
 5778 psi
<br>@Strain 0.290 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
45.46 MPa
<br>@Strain 0.900 %,<br> Temperature 90.0 °C
 6593 psi
<br>@Strain 0.900 %,<br> Temperature 194 °F
 ISO 11403-1 -2
46.09 MPa
<br>@Strain 3.43 %,<br> Temperature 150 °C
 6685 psi
<br>@Strain 3.43 %,<br> Temperature 302 °F
 ISO 11403-1 -2
51.17 MPa
<br>@Strain 0.390 %,<br> Temperature 23.0 °C
 7422 psi
<br>@Strain 0.390 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
58.2 MPa
<br>@Strain 7.82 %,<br> Temperature 150 °C
 8440 psi
<br>@Strain 7.82 %,<br> Temperature 302 °F
 ISO 11403-1 -2
65.07 MPa
<br>@Strain 1.82 %,<br> Temperature 90.0 °C
 9438 psi
<br>@Strain 1.82 %,<br> Temperature 194 °F
 ISO 11403-1 -2
68.87 MPa
<br>@Strain 0.610 %,<br> Temperature 40.0 °C
 9989 psi
<br>@Strain 0.610 %,<br> Temperature 104 °F
 ISO 11403-1 -2
87.33 MPa
<br>@Strain 5.93 %,<br> Temperature 90.0 °C
 12670 psi
<br>@Strain 5.93 %,<br> Temperature 194 °F
 ISO 11403-1 -2
95.95 MPa
<br>@Strain 0.600 %,<br> Temperature -40.0 °C
 13920 psi
<br>@Strain 0.600 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
99.27 MPa
<br>@Strain 0.830 %,<br> Temperature 23.0 °C
 14400 psi
<br>@Strain 0.830 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
100.21 MPa
<br>@Strain 0.800 %,<br> Temperature 0.000 °C
 14534 psi
<br>@Strain 0.800 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
116.09 MPa
<br>@Strain 0.870 %,<br> Temperature -20.0 °C
 16837 psi
<br>@Strain 0.870 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
141.6 MPa
<br>@Strain 2.70 %,<br> Temperature 40.0 °C
 20540 psi
<br>@Strain 2.70 %,<br> Temperature 104 °F
 ISO 11403-1 -2
164.13 MPa
<br>@Strain 2.40 %,<br> Temperature 23.0 °C
 23805 psi
<br>@Strain 2.40 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
191.12 MPa
<br>@Strain 2.25 %,<br> Temperature 0.000 °C
 27720 psi
<br>@Strain 2.25 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
214.94 MPa
<br>@Strain 2.14 %,<br> Temperature -20.0 °C
 31174 psi
<br>@Strain 2.14 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
221.48 MPa
<br>@Strain 1.82 %,<br> Temperature -40.0 °C
 32123 psi
<br>@Strain 1.82 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Elongation at Break 2.3 %
2.3 %
ISO 527-1/-2
Tensile Modulus 13.5 GPa
1960 ksi
ISO 527-1/-2
Secant Modulus 6.975 GPa
<br>@Strain 0.0400 %,<br> Temperature 40.0 °C
 1012 ksi
<br>@Strain 0.0400 %,<br> Temperature 104 °F
 ISO 11403-1 -2
7.08 GPa
<br>@Strain 1.90 %,<br> Temperature 40.0 °C
 1030 ksi
<br>@Strain 1.90 %,<br> Temperature 104 °F
 ISO 11403-1 -2
7.225 GPa
<br>@Strain 0.0400 %,<br> Temperature 23.0 °C
 1048 ksi
<br>@Strain 0.0400 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
7.825 GPa
<br>@Strain 0.0400 %,<br> Temperature 0.000 °C
 1135 ksi
<br>@Strain 0.0400 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
8.76 GPa
<br>@Strain 1.74 %,<br> Temperature 23.0 °C
 1270 ksi
<br>@Strain 1.74 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
9.625 GPa
<br>@Strain 0.0400 %,<br> Temperature -20.0 °C
 1396 ksi
<br>@Strain 0.0400 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
9.84 GPa
<br>@Strain 1.04 %,<br> Temperature 40.0 °C
 1430 ksi
<br>@Strain 1.04 %,<br> Temperature 104 °F
 ISO 11403-1 -2
10.25 GPa
<br>@Strain 0.0400 %,<br> Temperature -40.0 °C
 1487 ksi
<br>@Strain 0.0400 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
10.4 GPa
<br>@Strain 1.58 %,<br> Temperature 0.000 °C
 1510 ksi
<br>@Strain 1.58 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
10.7 GPa
<br>@Strain 0.140 %,<br> Temperature 40.0 °C
 1550 ksi
<br>@Strain 0.140 %,<br> Temperature 104 °F
 ISO 11403-1 -2
10.8 GPa
<br>@Strain 1.15 %,<br> Temperature 23.0 °C
 1570 ksi
<br>@Strain 1.15 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
11.4 GPa
<br>@Strain 1.67 %,<br> Temperature -20.0 °C
 1650 ksi
<br>@Strain 1.67 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
11.6 GPa
<br>@Strain 0.130 %,<br> Temperature 23.0 °C
 1690 ksi
<br>@Strain 0.130 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
11.7 GPa
<br>@Strain 0.370 %,<br> Temperature 40.0 °C
 1700 ksi
<br>@Strain 0.370 %,<br> Temperature 104 °F
 ISO 11403-1 -2
11.9 GPa
<br>@Strain 0.130 %,<br> Temperature 0.000 °C
 1720 ksi
<br>@Strain 0.130 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
12.2 GPa
<br>@Strain 0.990 %,<br> Temperature 0.000 °C
 1770 ksi
<br>@Strain 0.990 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
12.6 GPa
<br>@Strain 0.170 %,<br> Temperature -20.0 °C
 1830 ksi
<br>@Strain 0.170 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
12.7 GPa
<br>@Strain 1.17 %,<br> Temperature -20.0 °C
 1840 ksi
<br>@Strain 1.17 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
12.9 GPa
<br>@Strain 0.620 %,<br> Temperature 0.000 °C
 1870 ksi
<br>@Strain 0.620 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
13.0 GPa
<br>@Strain 0.480 %,<br> Temperature 23.0 °C
 1880 ksi
<br>@Strain 0.480 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
13.7 GPa
<br>@Strain 1.40 %,<br> Temperature -40.0 °C
 1980 ksi
<br>@Strain 1.40 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
13.7 GPa
<br>@Strain 0.130 %,<br> Temperature -40.0 °C
 1980 ksi
<br>@Strain 0.130 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved