Lanxess Pocan® C 1206 000000 PET + PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Lanxess Pocan® C 1206 000000 PET + PC.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
PET + PC, non-reinforced, injection molding, improved impact strengthInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ISO 1183
Bulk Density 0.800 g/cc
0.0289 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0070 cm/cm
0.0070 in/in
60x60x2; 270°C / WZ 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
0.0030 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0070 cm/cm
0.0070 in/in
60x60x2; 270°C / WZ 80°C; 600 bar; ISO 294-4
Melt Flow 30 g/10 min
<br>@Load 5.00 kg,<br> Temperature 260 °C
 30 g/10 min
<br>@Load 11.0 lb,<br> Temperature 500 °F
 ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO 527-1, -2; 50 mm/min
Elongation at Break 10 %
10 %
ISO 527-1, -2; 50 mm/min
Elongation at Yield 4.5 %
4.5 %
ISO 527-1, -2; 50 mm/min
Tensile Modulus 2.20 GPa
319 ksi
ISO 527-1, -2; 1 mm/min
Flexural Strength 75.0 MPa
<br>@Strain 5.00 %
 10900 psi
<br>@Strain 5.00 %
 2 mm/min; ISO 178-A
Flexural Yield Strength 65.0 MPa
<br>@Strain 3.50 %
 9430 psi
<br>@Strain 3.50 %
 2 mm/min; ISO 178-A
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 15.0 kJ/m²
<br>@Temperature -30.0 °C
 7.14 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 180-1A
50.0 kJ/m²
<br>@Temperature 23.0 °C
 23.8 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) NB
<br>@Temperature 23.0 °C
 NB
<br>@Temperature 73.4 °F
 ISO 180-1U
NB
<br>@Temperature -30.0 °C
 NB
<br>@Temperature -22.0 °F
 ISO 180-1U
Charpy Impact Unnotched NB
<br>@Temperature 23.0 °C
 NB
<br>@Temperature 73.4 °F
 ISO 179-1eU
NB
<br>@Temperature -30.0 °C
 NB
<br>@Temperature -22.0 °F
 ISO 179-1eU
Charpy Impact, Notched 2.00 J/cm²
<br>@Temperature -30.0 °C
 9.52 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 179-1eA
5.50 J/cm²
<br>@Temperature 23.0 °C
 26.2 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 80.0 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 44.4 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 250 °C
482 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
ISO 75-1, -2
Vicat Softening Point 130 °C
<br>@Load 5.10 kg
 266 °F
<br>@Load 11.2 lb
 120°C/hour; ISO 306
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
admissible residence time at Tmax &lt;= 10 min
270 °C
518 °F
for test specimens; ISO 294
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
80.0 °C
176 °F
for test specimens; ISO 294
Drying Temperature 120 °C
248 °F
Dry Time 4 - 8 hour
4 - 8 hour
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 7792-1-PET+PC, GHMPR, 09-020