Lanxess Pocan® B 1701 000000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® B 1701 000000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, extrusion, food contactInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ISO 1183 |
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.020 cm/cm | 0.020 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.020 cm/cm | 0.020 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 | |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 260 °C |
12 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1, -2; 50 mm/min |
| Elongation at Break | >= 20 % | >= 20 % | ISO 527-1, -2; 50 mm/min |
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527-1, -2; 50 mm/min |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 85.0 MPa @Strain 6.00 % |
12300 psi @Strain 6.00 % |
2 mm/min; ISO 178-A |
| Flexural Yield Strength | 75.0 MPa @Strain 3.50 % |
10900 psi @Strain 3.50 % |
2 mm/min; ISO 178-A |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180-1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180-1U | |
| Charpy Impact Unnotched | 20.0 J/cm² @Temperature -30.0 °C |
95.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C @Temperature 23.0 - 55.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 23.0 - 55.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1, -2 |
| Vicat Softening Point | 180 °C @Load 5.10 kg |
356 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | <= 1.00e+15 ohm | <= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm @Thickness 1.00 mm |
762 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.0015 @Frequency 100 Hz |
0.0015 @Frequency 100 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | for test specimens; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 - 8 hour | 4 - 8 hour | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 7792-1-PBT, GM, 13-030 |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals Silicon Iron FS-1603 Powdered Metal
- SABIC Innovative Plastics LNP STAT-KON Cycoloy_JK800 PC+ABS
- SABIC Innovative Plastics Valox® HX312C PBT (Europe-Africa-Middle East)
- Saint-Gobain CHR® T Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Borealis Borecene™ RM8342RC Linear Polyethylene for Rotational Molding
- Chase Plastics CP Pryme® AH300 Acetal Homopolymer, Recycled Content
- BASF Ultramid® B40 PA6
- 3M Scotch-Weld™ CA50 Gel Instant Adhesive
- ACC QM 113 QSI Quantum Silicones 13 Durometer Condensation Cured Moldmaking Material
- Overview of materials for Polyethersulfone (PES)
Copyright © lookpolymers.com All Rights Reserved