Techmer ES Plastiblend® APC100 UV
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Techmer ES |
| Trade Name | Plastiblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plastiblend® APC100 UV.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV ResistanceInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 5.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 16 g/10 min @Load 5.00 kg, Temperature 260 °C |
16 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 45.5 MPa | 6600 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 6.94 J/cm @Thickness 3.17 mm |
13.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY201 PC+ABS (Europe-Africa-Middle East)
- Covestro Petlon® 8535 Semi-Crystalline PET, 35% Mineral/Glass Fiber (discontinued **)
- ExxonMobil ESCOR™ AT 325 Molding, extrusion and compounding resin (discontinued **)
- H.C. Starck Amperit® 587.09 Chromium Carbide-Nickel Chromium (Cr3C2-NiCr)
- Gouda Vuurvast CURON 150 HR GM Dense Refractory Castable
- Momentive Performance Materials Addisilâ„¢ 1040 E Industrial Extrusion Heat Cured Rubber
- A. Schulman LP552-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- DuPont Teijin Films Mylar® RL4 Polyester Packaging Film, 100 Gauge
- 3M 9552 Adhesive Transfer Tapes with Adhesive 220
Copyright © lookpolymers.com All Rights Reserved