Seals Eastern 7265 Fluorocarbon-Elastomer
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 7265 Fluorocarbon-Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Seals Eastern's formulated Viton® elastomers can be utilized in seals, o-rings, gaskets, packings and other applications where thermal stability and chemical resistance are required.Features:Viton ETPBroad chemical resistantViton® is a registered trademark of DuPont. Information provided by Seals Eastern.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | ASTM D297, 15 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 84 | >= 84 | ASTM D2240 |
| 88 | 88 | Average; ASTM D2240 | |
| Tensile Strength | >= 13.1 MPa | >= 1900 psi | ASTM D412 Method A |
| 16.4 MPa | 2380 psi | Average; ASTM D412 Method A | |
| Tensile Stress | 4.65 MPa @Strain 25.0 % |
675 psi @Strain 25.0 % |
Average; ASTM D412 Method A |
| >= 6.21 MPa @Strain 50.0 % |
>= 900 psi @Strain 50.0 % |
ASTM D412 Method A | |
| 7.412 MPa @Strain 50.0 % |
1075 psi @Strain 50.0 % |
Average; ASTM D412 Method A | |
| >= 8.96 MPa @Strain 100 % |
>= 1300 psi @Strain 100 % |
ASTM D412 Method A | |
| 11.20 MPa @Strain 100 % |
1625 psi @Strain 100 % |
Average; ASTM D412 Method A | |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D412 Method A |
| 200 % | 200 % | Average; ASTM D412 Method A | |
| Modulus of Elasticity | 0.02948 GPa | 4.275 ksi | Calculated; ASTM D412 Method A |
| Shear Modulus | 0.009825 GPa | 1.425 ksi | Calculated; ASTM D412 Method A |
| Secant Modulus | 0.02771 GPa | 4.019 ksi | ASTM D412 Method A |
| Tear Strength Test | 146 | 146 | psi; ASTM D624, Die B |
| Compression Set | 44 % @Temperature 200 °C, Time 252000 sec |
44 % @Temperature 392 °F, Time 70.0 hour |
ASTM D395, Test B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 93.3 °C | 200 °F | |
| Glass Transition Temp, Tg | -21.1 °C | -6.00 °F | ASTM D1329 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 240 Month | 240 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy/ Unit Volume at 20% Elongation (psi) | 76 | ASTM D412 Method A |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer
- Nilit FRIANYL B63 H-GV35 Nylon 6 for injection molding, 35% glass fiber reinforced
- Solvay IGEPAL® CO 520 Surfactant
- A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66
- Eurostar Staramide AG5K PA66, 25% Glass Filled, Injection Molded
- Asahi Kasei Thermylene® P6-30FG-0632 30% Glass Fiber Reinforced, Heat Stabilized
- BASF Propionaldehyde
- Solvay TECHNYL® 1021GF6 PA6, 30% glass fiber, Conditioned
- Solvay Specialty Polymers Ixef® 5002 Polyarylamide (PARA), 20% GlassPTFE (discontinued **)
- PSM Industries PolyAlloys WNF-5421 Tungsten Heavy Alloy
Copyright © lookpolymers.com All Rights Reserved