Lanxess Durethan® DP AKV 30 HR EF 901510 Nylon 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP AKV 30 HR EF 901510 Nylon 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding grade, 30% glass fibers, good heat-ageing resistance and hydrolysis resistance, good flowability (Easy Flow)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0037 cm/cm | 0.0037 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | ISO 294-4, 2577 |
| Melt Flow | 28 g/10 min @Load 5.00 kg, Temperature 270 °C |
28 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
| 155 MPa | 22500 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.2 % | 3.2 % | ISO 527-1/-2 |
| 8.0 % | 8.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 5.30 GPa | 769 ksi | Conditioned; ISO 527-1/-2 |
| 8.80 GPa | 1280 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Impact | 774 | 774 | Puncture maximum force (N); ISO 6603-2 |
| 756 @Temperature -30.0 °C |
756 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.70 J | 1.99 ft-lb | ISO 6603-2 |
| 2.50 J @Temperature -30.0 °C |
1.84 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.50 J @Temperature -30.0 °C |
1.84 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 250 °C | >= 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MWHR,14-090,GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® GM-1224-A Butene LLDPE Masterbatch Resin
- Dielectric Polymers NT-511 High Temperature Tape (discontinued **)
- Polymer Resources NY66-GP2 General Purpose Nylon 66, Nucleated
- Technetics Group Texolon™ 9406 PTFE (Unverified Data**)
- SSAB Tunnplat Domex® 034 BOR Rolled Boron Steel
- Silberline Sparkle Silvet® 970-20-J
- Zircar Zirconia FBD Zirconia Boards, Discs, and Cylinders Insulation
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- 3M Scotchcal™ 3690 Graphic Film
- ATI Allegheny Ludlum Grade 4 Titanium (UNS R50700)
Copyright © lookpolymers.com All Rights Reserved