Lanxess Durethan® BKV 50 H2.0 EF 900116 Nylon 6, 50% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 50 H2.0 EF 900116 Nylon 6, 50% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, injection molding grade, 50% glass fibers, good heat-ageing resistance, low viscosity (easy flow)Application Examples: mirror baseplates
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0019 cm/cm
0.0019 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0051 cm/cm
0.0051 in/in
ISO 294-4, 2577
Melt Flow 36 g/10 min

@Load 5.00 kg,
Temperature 270 °C
 36 g/10 min

@Load 11.0 lb,
Temperature 518 °F
 Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
Conditioned; ISO 527-1/-2
225 MPa
32600 psi
ISO 527-1/-2
Elongation at Break 2.3 %
2.3 %
ISO 527-1/-2
3.5 %
3.5 %
Conditioned; ISO 527-1/-2
Tensile Modulus 10.0 GPa
1450 ksi
Conditioned; ISO 527-1/-2
16.5 GPa
2390 ksi
ISO 527-1/-2
Charpy Impact Unnotched 8.50 J/cm²

@Temperature 23.0 °C
 40.4 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179/1eU
8.50 J/cm²

@Temperature -30.0 °C
 40.4 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179/1eU
9.50 J/cm²

@Temperature -30.0 °C
 45.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
9.50 J/cm²

@Temperature 23.0 °C
 45.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Impact 1179
1179
Puncture maximum force (N); ISO 6603-2
1000

@Temperature -30.0 °C
 1000

@Temperature -22.0 °F
 Puncture maximum force (N); ISO 6603-2
Puncture Energy 4.30 J
3.17 ft-lb
ISO 6603-2
3.40 J

@Temperature -30.0 °C
 2.51 ft-lb

@Temperature -22.0 °F
 ISO 6603-2
3.40 J

@Temperature -30.0 °C
 2.51 ft-lb

@Temperature -22.0 °F
 Conditioned; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359-1/-2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 213 °C
415 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 180 °C
356 °F
ISO 75-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 4.00e+11 ohm-cm
4.00e+11 ohm-cm
Conditioned; IEC 60093
7.00e+14 ohm-cm
7.00e+14 ohm-cm
IEC 60093
Dielectric Constant 4.2

@Frequency 1.00e+6 Hz
 4.2

@Frequency 1.00e+6 Hz
 IEC 60250
4.7

@Frequency 100 Hz
 4.7

@Frequency 100 Hz
 IEC 60250
4.8

@Frequency 1.00e+6 Hz
 4.8

@Frequency 1.00e+6 Hz
 Conditioned; IEC 60250
12.9

@Frequency 100 Hz
 12.9

@Frequency 100 Hz
 Conditioned; IEC 60250
Dielectric Strength 34.0 kV/mm
864 kV/in
Conditioned; IEC 60243-1
35.0 kV/mm
889 kV/in
IEC 60243-1
Dissipation Factor 0.0135

@Frequency 100 Hz
 0.0135

@Frequency 100 Hz
 IEC 60250
0.017

@Frequency 1.00e+6 Hz
 0.017

@Frequency 1.00e+6 Hz
 IEC 60250
0.0774

@Frequency 1.00e+6 Hz
 0.0774

@Frequency 1.00e+6 Hz
 Conditioned; IEC 60250
0.2622

@Frequency 100 Hz
 0.2622

@Frequency 100 Hz
 Conditioned; IEC 60250
Comparative Tracking Index 400 V
400 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Features Heat stabilized or stable to heat
Form Pellets
ISO Shortname ISO1874-PA6, MHR, 10-160, GF50
Processing Injection molding