LATI Latilub 62-10T PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 62-10T PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyamide 6 (PA6). PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Linear Mold Shrinkage, Flow 0.0095 - 0.0125 cm/cm
0.0095 - 0.0125 in/in
Linear Mold Shrinkage, Transverse 0.010 - 0.0135 cm/cm
0.010 - 0.0135 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
Elongation at Break 20 %
20 %
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 2.70 GPa
392 ksi
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Coefficient of Friction, Dynamic 0.22
0.22
Coefficient of Friction, Static 0.25
0.25
K (wear) Factor 9.30 x 10-8 mm³/N-M
4.62 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 170 °C
338 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 195 °C

@Load 5.00 kg
383 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 230 - 250 °C
446 - 482 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa