Lanxess Durethan® BKV 35 CX H2.0 900876 Nylon 6, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 35 CX H2.0 900876 Nylon 6, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 35% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00050 cm/cm | 0.00050 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0015 cm/cm | 0.0015 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0070 cm/cm | 0.0070 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 180 MPa | 26100 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 3.0 % | 3.0 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 5.5 % | 5.5 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 6.50 GPa | 943 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 10.5 GPa | 1520 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 280 MPa @Strain 4.00 % |
40600 psi @Strain 4.00 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Yield Strength | 270 MPa @Strain 3.50 % |
39200 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Modulus | 10.0 GPa | 1450 ksi | d.a.m., 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1U |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| 270 °C | 518 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6, GHR, 10-100, GF35 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9930 TPE, ABS/PC Overmold
- Resinlab® CYNERGY CA6006 Adhesive
- Mallard Creek Polymers ROVENE® 4848 SBR Emulsion
- LG Chemical BM662 ABS, Heat Resistance
- SABIC Innovative Plastics LNP LUBRICOMP NXCY620 PC+ABS
- SABIC Innovative Plastics Ultem DT1800E PEI Blend (Asia Pacific)
- Cotronics Duralco™ 4461 Electrically Resistant, Low Viscosity Epoxy Adhesive, Coating, and Sealant
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Hi-Sil 233 Filler
- Termopol Termoton® K2GA4055D TPE Compound, based on SEBS and Polyolefins
Copyright © lookpolymers.com All Rights Reserved