- Lanxess Durethan® BKV 30 G W1 901317 Nylon 6, Glass Fiber Reinforced
Lanxess Durethan® BKV 30 G W1 901317 Nylon 6, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 30 G W1 901317 Nylon 6, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glass fibers, injection molding, weather stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.365 g/cc | 1.365 g/cc | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 6.4 % | 6.4 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0060 cm/cm | 0.0060 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 209 MPa | 30300 psi | ISO 2039-1 |
| Tensile Strength at Break | 106 MPa | 15400 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 180 MPa | 26100 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 2.7 % | 2.7 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 6.1 % | 6.1 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 6.60 GPa | 957 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 9.90 GPa | 1440 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 177 MPa @Strain 5.70 % |
25700 psi @Strain 5.70 % |
cond., 2 mm/min; ISO 178-A |
| 270 MPa @Strain 3.70 % |
39200 psi @Strain 3.70 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 156 MPa @Strain 3.50 % |
22600 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 260 MPa @Strain 3.50 % |
37700 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 6.30 GPa | 914 ksi | cond., 2 mm/min; ISO 178-A |
| 8.70 GPa | 1260 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | d.a.m.; ISO 180-1A |
| 10.0 kJ/m² | 4.76 ft-lb/in² | cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1U |
| 45.0 kJ/m² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1U | |
| 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U | |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1U | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eU |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| Puncture Energy | 2.00 J @Load <=75.5 kg, Temperature -30.0 °C |
1.48 ft-lb @Load <=166 lb, Temperature -22.0 °F |
ISO 6603-2 |
| 3.00 J @Load <=85.7 kg, Temperature 23.0 °C |
2.21 ft-lb @Load <=189 lb, Temperature 73.4 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 219 °C | 426 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1, -2 |
| Vicat Softening Point | 211 °C @Load 5.10 kg |
412 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 500 V | 500 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability Test | passed | ISO 3795; US-FMVSS302 |
| ISO Shortname | ISO 1874-PA 6, GLR, 14-100, GF30 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® MC8002 PC+ABS (Asia Pacific)
- Kinlead LSD11 Low Temperature Grade Heat Sealable Film (thickness: 25 µm)
- Gouda Vuurvast CURON 160 HS GM Dense Refractory Castable
- SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT (Europe-Africa-Middle East)
- CoorsTek ADS-96R 96% Alumina Thick Film Substrate
- Chosun Refractories HSC-15 Dense and High-Strength Castable, Credens
- Arkema Group Pebax® 2533 SN 01 Polyether Block Amide (PEBA) (Conditioned)
- Aremco Corr-Paint™ CP4080 High Temperature Protective Coating Silicone, Aluminum Filled
- Addiplast Addinyl A2 X Nylon 66
Copyright © lookpolymers.com All Rights Reserved