TPI Porene® ABS-GA803 High Gloss, UV Resistant ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Thai Petrochemical Industry Co. LTD. |
| Trade Name | Porene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TPI Porene® ABS-GA803 High Gloss, UV Resistant ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 10.0 kg, Temperature 220 °C |
18 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 42.7 MPa @Thickness 3.17 mm |
6190 psi @Thickness 0.125 in |
|
| Flexural Yield Strength | 58.6 MPa @Thickness 3.17 mm |
8500 psi @Thickness 0.125 in |
|
| Flexural Modulus | 2.15 GPa @Thickness 3.17 mm |
312 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 2.40 J/cm @Thickness 6.35 mm |
4.50 ft-lb/in @Thickness 0.250 in |
|
| 2.67 J/cm @Thickness 3.17 mm |
5.00 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 232 °C | 450 °F | |
| Melt Temperature | 218 - 260 °C | 425 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Mitsui Fybrel® E 990 Polyolefin Synthetic Pulp, Dry Processes (discontinued **)
- Huntsman PE2018 Injection Molding Polyethylene (discontinued **)
- Karina KAPU 6535/1-Y Ivory PVC Compound
- Kinlead LSD11 Low Temperature Grade Heat Sealable Film (thickness: 20 µm)
- A. Schulman POLYBATCH™ FSU-105 Concentrate Based In LDPE
- Cossa Polimeri ESTAPROP HK 2540 T8 Polypropylene, 20% Mineral Filled
- Covestro Bayblend® FR 90 N Polycarbonate/ABS Blend
- Covestro Makrolon® 6267 Polycarbonate, Flame Retardant Grade
- ChevronTexaco Texcool® E 100
- Ineos H35G-01 Polypropylene Homopolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved