- Lehmann & Voss LUVOCOM® 80-8003 Polyacetal-copolymer, with carbon fiber
Lehmann & Voss LUVOCOM® 80-8003 Polyacetal-copolymer, with carbon fiber
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-8003 Polyacetal-copolymer, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.No change of electric potential at bearings in case of separation of charge caused by transport and guiding of paper and foil.Bearings, sleeves, control disks, gear wheels, cams.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | |
| Melt Flow | 2.86 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.86 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 48.0 MPa | 6960 psi | |
| Elongation at Yield | 0.80 % | 0.80 % | |
| 1.1 % | 1.1 % | flexural | |
| Modulus of Elasticity | 9.50 GPa | 1380 ksi | |
| Flexural Strength | 65.0 MPa | 9430 psi | |
| Flexural Modulus | 8.00 GPa | 1160 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Vicat Softening Point | 165 °C | 329 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10 ohm | <= 10 ohm | |
| Insulation Resistance | <= 10 ohm | <= 10 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1332L Polycarbonate, UV Stabilized, Unreinforced
- Hybrid Plastics Fireban® Mark VII-IS Resorcinolinic (PRF)
- LG Chemical 95HCTC SAN, High Transparency, Heat Resistance, Chemical Resistance
- Indium Corp. Indalloy 221 Silver Solder Alloy
- Gromax BFG30-DN00N1 Nylon 6 30% Glass Filled (Dry)
- Solvay ALKAMULS® S 85 Surfactant
- Hexcel® Redux® 335U Adhesive film for bonding metallic and composite components (0.06 psf)
- Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced
- Arlon 30850S125 0.125" Uncured, Unsupported Silicone Rubber on a Kodacel Carrier
- Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved