- Lanxess Durethan® BKV 130 H3.0 DUS008 000000 Nylon 6, 30% Glass Fiber
Lanxess Durethan® BKV 130 H3.0 DUS008 000000 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Filled, Impact Grade , Nylon 6, Heat Stabilized |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 130 H3.0 DUS008 000000 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, glass fiber, injection molding, impact modified, heat-aged stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.365 g/cc | 0.04931 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | conditioned, 5 mm/min; ISO 527-1,-2 |
| 160 MPa | 23200 psi | 5 mm/min; ISO 527-1,-2 | |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527-1,-2 |
| 7.0 % | 7.0 % | conditioned, 5 mm/min; ISO 527-1,-2 | |
| Tensile Modulus | 5.20 GPa | 754 ksi | conditioned, 1 mm/min; ISO 527-1,-2 |
| 9.00 GPa | 1310 ksi | 1 mm/min; ISO 527-1,-2 | |
| Flexural Strength | 145 MPa | 21000 psi | conditioned, 2 mm/min; ISO 178-A |
| 250 MPa | 36300 psi | 2 mm/min; ISO 178-A | |
| Flexural Modulus | 4.80 GPa | 696 ksi | conditioned, 2 mm/min; ISO 178-A |
| 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178-A | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
conditioned; ISO 179-1eU | |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
conditioned; ISO 179-1eA | |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | |
| 2.80 J/cm² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 2.00 - 6.00 hour @Temperature 80.0 °C |
2.00 - 6.00 hour @Temperature 176 °F |
|
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer test |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 66 GF 30 TS 002 PA66 reinforced with glass fiber, heat stabilized
- Shuman 502C Black Polypropylene Copolymer
- Teijin Panlite® LV-2225Y Standard (mold release/ice color grade) Polycarbonate Resin
- Teknor Apex MF 826 Polyvinyl Chloride, Flexible Film
- ExxonMobil 447 Mobilmet 440 Series
- ExxonMobil Mobil Permazone 50/50 Prediluted Coolant/Antifreeze
- Tra-Con Tra-Bond 526W01 Microelectronics Grade Encapsulant
- DSM Stanyl® TW363 (COND) Nylon 46 Heat Stabilized, Impact Modified (North America)
- Arkema Group Rilsan® BECN W3 TL Nylon 11, Sheathing Grade (Dry)
Copyright © lookpolymers.com All Rights Reserved