DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass Reinforced Polyamide 6Zytel 73G30L NC010 is a 30% glass fiber reinforced polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
DAM; ISO 1183
Water Absorption 6.3 %

@Thickness 2.00 mm
 6.3 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.90 %

@Thickness 2.00 mm
 1.90 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 150 cm³/g
150 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
50%RH; ISO 527-1/-2
185 MPa
26800 psi
DAM; ISO 527-1/-2
Tensile Stress 5.50 MPa

@Strain 0.110036 %,
Time 36000 sec
 798 psi

@Strain 0.110036 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
5.50 MPa

@Strain 0.0989091 %,
Time 3600 sec
 798 psi

@Strain 0.0989091 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
5.50 MPa

@Strain 0.134764 %,
Time 3.60e+6 sec
 798 psi

@Strain 0.134764 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
5.50 MPa

@Strain 0.148364 %,
Time 3.60e+7 sec
 798 psi

@Strain 0.148364 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
5.50 MPa

@Strain 0.121164 %,
Time 360000 sec
 798 psi

@Strain 0.121164 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
22.0 MPa

@Strain 0.531636 %,
Time 360000 sec
 3190 psi

@Strain 0.531636 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
22.0 MPa

@Strain 0.635491 %,
Time 3.60e+7 sec
 3190 psi

@Strain 0.635491 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
22.0 MPa

@Strain 0.582327 %,
Time 3.60e+6 sec
 3190 psi

@Strain 0.582327 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
22.0 MPa

@Strain 0.433964 %,
Time 3600 sec
 3190 psi

@Strain 0.433964 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
22.0 MPa

@Strain 0.480945 %,
Time 36000 sec
 3190 psi

@Strain 0.480945 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
44.0 MPa

@Strain 1.27345 %,
Time 36000 sec
 6380 psi

@Strain 1.27345 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
44.0 MPa

@Time 3600 sec,
Strain 1.15971 %
 6380 psi

@Time 1.00 hour,
Strain 1.15971 %
 50%RH; isochronous; ISO 11403-1 -2
44.0 MPa

@Strain 1.48364 %,
Time 3.60e+6 sec
 6380 psi

@Strain 1.48364 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
44.0 MPa

@Strain 1.58255 %,
Time 3.60e+7 sec
 6380 psi

@Strain 1.58255 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
44.0 MPa

@Strain 1.38473 %,
Time 360000 sec
 6380 psi

@Strain 1.38473 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break 3.5 %
3.5 %
DAM; ISO 527-1/-2
6.0 %
6.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 6.00 GPa
870 ksi
50%RH; ISO 527-1/-2
9.80 GPa
1420 ksi
DAM; ISO 527-1/-2
Flexural Modulus 8.20 GPa
1190 ksi
DAM; ISO 178
Shear Modulus 0.586 GPa

@Temperature 160 °C
 85.0 ksi

@Temperature 320 °F
 DAM; Dynamic; ISO 11403-1 -2
0.6285 GPa

@Temperature 120 °C
 91.16 ksi

@Temperature 248 °F
 DAM; Dynamic; ISO 11403-1 -2
0.817 GPa

@Temperature 70.0 °C
 118 ksi

@Temperature 158 °F
 DAM; Dynamic; ISO 11403-1 -2
1.857 GPa

@Temperature 20.0 °C
 269.3 ksi

@Temperature 68.0 °F
 DAM; Dynamic; ISO 11403-1 -2
1.975 GPa

@Temperature -20.0 °C
 286.5 ksi

@Temperature -4.00 °F
 DAM; Dynamic; ISO 11403-1 -2
2.081 GPa

@Temperature -50.0 °C
 301.8 ksi

@Temperature -58.0 °F
 DAM; Dynamic; ISO 11403-1 -2
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
DAM; ISO 180/1A
20.0 kJ/m²
9.52 ft-lb/in²
50%RH; ISO 180/1A
11.0 kJ/m²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 180/1A
11.0 kJ/m²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 180/1A
11.0 kJ/m²

@Temperature -40.0 °C
 5.23 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) 100 kJ/m²
47.6 ft-lb/in²
DAM; ISO 180/1U
90.0 kJ/m²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 180/1U
Charpy Impact Unnotched 9.70 J/cm²
46.2 ft-lb/in²
50%RH; ISO 179/1eU
10.0 J/cm²
47.6 ft-lb/in²
DAM; ISO 179/1eU
8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eU
8.40 J/cm²

@Temperature -30.0 °C
 40.0 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
DAM; ISO 179/1eA
2.30 J/cm²
10.9 ft-lb/in²
50%RH; ISO 179/1eA
1.10 J/cm²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
1.10 J/cm²

@Temperature -40.0 °C
 5.23 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 179/1eA
2.10 J/cm²

@Temperature -30.0 °C
 9.99 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 2590 MPa

@Pressure 30.0 MPa,
Temperature 100 °C
 375000 psi

@Pressure 4350 psi,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2690 MPa

@Pressure 25.0 MPa,
Temperature 100 °C
 391000 psi

@Pressure 3630 psi,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2816.9 MPa

@Pressure 20.0 MPa,
Temperature 100 °C
 408560 psi

@Pressure 2900 psi,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2900 MPa

@Pressure 15.0 MPa,
Temperature 100 °C
 421000 psi

@Pressure 2180 psi,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2940 MPa

@Pressure 10.0 MPa,
Temperature 100 °C
 427000 psi

@Pressure 1450 psi,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2960 MPa

@Pressure 5.00 MPa,
Temperature 100 °C
 429000 psi

@Pressure 725 psi,
Temperature 212 °F
 DAM; ISO 11403-1 -2
3110 MPa

@Pressure 55.0 MPa,
Temperature 23.0 °C
 451000 psi

@Pressure 7980 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3420 MPa

@Pressure 50.0 MPa,
Temperature 23.0 °C
 496000 psi

@Pressure 7250 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3640 MPa

@Pressure 36.0 MPa,
Temperature 90.0 °C
 527000 psi

@Pressure 5220 psi,
Temperature 194 °F
 DAM; ISO 11403-1 -2
3680 MPa

@Pressure 35.0 MPa,
Temperature 90.0 °C
 534000 psi

@Pressure 5080 psi,
Temperature 194 °F
 DAM; ISO 11403-1 -2
3850 MPa

@Pressure 60.0 MPa,
Temperature 60.0 °C
 558000 psi

@Pressure 8700 psi,
Temperature 140 °F
 DAM; ISO 11403-1 -2
3919.9 MPa

@Pressure 30.0 MPa,
Temperature 90.0 °C
 568530 psi

@Pressure 4350 psi,
Temperature 194 °F
 DAM; ISO 11403-1 -2
3950 MPa

@Pressure 50.0 MPa,
Temperature 60.0 °C
 573000 psi

@Pressure 7250 psi,
Temperature 140 °F
 DAM; ISO 11403-1 -2
4010 MPa

@Pressure 40.0 MPa,
Temperature 60.0 °C
 582000 psi

@Pressure 5800 psi,
Temperature 140 °F
 DAM; ISO 11403-1 -2
4050 MPa

@Pressure 40.0 MPa,
Temperature 23.0 °C
 587000 psi

@Pressure 5800 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2