Lanxess Durethan® BC 304 H3.0 000000 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BC 304 H3.0 000000 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, non-reinforced, elastomer-modified, extremely high notched impact strength, including in the dry state and at low temperatures, also applicable for barrier layers in extrusion blow molded containers for e.g. agrochemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Water Absorption | 7.5 % | 7.5 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | Conditioned; ISO 527-1/-2 |
| 45.0 MPa | 6530 psi | ISO 527-1/-2 | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 |
| >= 50 % | >= 50 % | Nominal, Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-1/-2 |
| 30 % | 30 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 0.800 GPa | 116 ksi | Conditioned; ISO 527-1/-2 |
| 1.80 GPa | 261 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 12.0 J/cm² @Temperature 23.0 °C |
57.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Puncture Energy | 120 J | 88.5 ft-lb | ISO 6603-2 |
| 125 J | 92.2 ft-lb | Conditioned; ISO 6603-2 | |
| 125 J @Temperature -30.0 °C |
92.2 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 125 J @Temperature -30.0 °C |
92.2 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 160 µm/m-°C | 88.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 40.0 °C | 104 °F | ISO 75-1/-2 |
| Vicat Softening Point | 150 °C | 302 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 21 % | 21 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 100 Hz |
3.3 @Frequency 100 Hz |
IEC 60250 | |
| 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 11 @Frequency 100 Hz |
11 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.0070 @Frequency 100 Hz |
0.0070 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.090 @Frequency 1.00e+6 Hz |
0.090 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.175 @Frequency 100 Hz |
0.175 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | High impact or high impact modified | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MPR,-020N | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Covestro Apec® DP 1-9339/5 Polycarbonate (discontinued **)
- Lanxess Pocan® T 7323 000000 PBT + PET, 20% Glass Fiber
- Haynes 242® alloy, bar and rings, annealed and aged
- SABIC Innovative Plastics ULTEM 2100R PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-KON DEL13EXC PC (Asia Pacific)
- Saint-Gobain CHR® K290ESD Polyimide Film Backing Silicone Adhesive Pressure Sensitive Tape
- Borealis BorPURE™ RE216CF Polypropylene Random Copolymer
- CP-Polymer-Technik Wellamid® 6000/50 CP Nylon 6, Impact Modified Until 0°C, Dry
- China Tungsten YG9 Tungsten Carbide
- 3M 3W25X Protective UV Tape
Copyright © lookpolymers.com All Rights Reserved