Lanxess Durethan® B 35 F 000000 Nylon 6, Extrusion, Low Viscosity
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® B 35 F 000000 Nylon 6, Extrusion, Low Viscosity.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, non-reinforced, extrusion, low viscosity, no additivesInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 10 % | 10 % | ISO 62 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | cond.; ISO 527-1, -2; 50 mm/min |
| 75.0 MPa | 10900 psi | d.a.m.; ISO 527-1, -2; 50 mm/min | |
| Elongation at Break | 20 % | 20 % | d.a.m.; ISO 527-1, -2; 50 mm/min |
| >= 50 % | >= 50 % | cond.; ISO 527-1, -2; 50 mm/min | |
| Elongation at Yield | 4.0 % | 4.0 % | d.a.m.; ISO 527-1, -2; 50 mm/min |
| 25 % | 25 % | cond.; ISO 527-1, -2; 50 mm/min | |
| Tensile Modulus | 0.800 GPa | 116 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 2.80 GPa | 406 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 20.0 MPa @Strain 3.50 % |
2900 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 90.0 MPa @Strain 3.50 % |
13100 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 0.700 GPa | 102 ksi | cond., 2 mm/min; ISO 178-A |
| 2.60 GPa | 377 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A | |
| 7.50 kJ/m² @Temperature -30.0 °C |
3.57 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1A | |
| 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | <= 0.500 J/cm² @Temperature -30.0 °C |
<= 2.38 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA | |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 40.0 °C | 104 °F | |
| Vicat Softening Point | 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 24 % | 24 % | Method A; ISO 4589-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | cond.; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | d.a.m.; IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | cond.; IEC 60093 |
| 1.00e+14 ohm | 1.00e+14 ohm | d.a.m.; IEC 60093 | |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
d.a.m.; IEC 60250 | |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 18 @Frequency 100 Hz |
18 @Frequency 100 Hz |
cond.; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm @Thickness 1.00 mm |
762 kV/in @Thickness 0.0394 in |
d.a.m.; IEC 60243-1 |
| 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
cond.; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | for test specimens; ISO 294 |
| Mold Temperature | 40.0 °C | 104 °F | for test specimens; ISO 294 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6, E, 18-030 |
Users viewing this material also viewed the following:
- MetalTek MTEK 85-5-5-5 Cast UNS C83600 Bearing Bronze
- SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-KON RE007 PA 66
- Chase Plastics CP Pryme® PC100R Polycarbonate Molding Resin, Mold Release
- Diamond Polymers ABS 2501 Injection Molding Grade, Medium Impact, High Flow
- ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 10% cold work (ASTM XM-8; UNS S43035)
- Wanhua Chemical Wanthane® WHT-1185 Polyester Based TPU
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.25 PHR Zinc Stearate
Copyright © lookpolymers.com All Rights Reserved