LTL Color Compounds ColorFast® PBA2000 PBT/ABS Alloy, Flame Retarded
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® PBA2000 PBT/ABS Alloy, Flame Retarded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame-retarded V0-rated PBT/ABS alloyAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.3 MPa | 5700 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 21.4 MPa | 3100 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 13 % | 13 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.21 GPa | 320 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-0 @Thickness 1.30 mm |
V-0 @Thickness 0.0512 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 238 °C | 400 - 460 °F | |
| Middle Barrel Temperature | 210 - 232 °C | 410 - 450 °F | |
| Front Barrel Temperature | 221 - 254 °C | 430 - 490 °F | |
| Nozzle Temperature | 216 - 249 °C | 420 - 480 °F | |
| Melt Temperature | 221 - 254 °C | 430 - 490 °F | |
| Mold Temperature | 10.0 - 71.1 °C | 50.0 - 160 °F | |
| Drying Temperature | 85.0 °C | 185 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Polykemi AB POLYasa 3010F Extra High Flow ASA
- SABIC Innovative Plastics LNP Faradex NS0029 PC+ABS (Europe-Africa-Middle East)
- Polykemi AB POLYfill PPH GF5040 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Kolon NOPLA® KE131 PEN-PET Copolyester
- Solvay TECHNYL® A 221 Natural FA PA66, Conditioned
- Techmer ES HiFill FR® PC FR
- ThyssenKrupp TBL Structural Steel
- Hexcel® HexWeb® CR III 1/16-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Trelleborg R449 Natural Rubber Polyisoprene
- China Tungsten YG4C Tungsten Carbide
Copyright © lookpolymers.com All Rights Reserved