LTL Color Compounds ColorFast® FRPC400 Polycarbonate, Flame-Retarded
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRPC400 Polycarbonate, Flame-Retarded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame-retarded V0, high impact injection molding polycarbonateAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | 0.125; ASTM D955 |
| Melt Flow | 11 g/10 min @Load 1.20 kg, Temperature 300 °C |
11 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 70 | 70 | ASTM D785 |
| Tensile Strength at Break | 55.2 MPa | 8000 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 90 % | 90 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 91.0 MPa | 13200 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Temperature 22.8 °C |
12.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 - 250 V @Thickness 3.00 mm |
175 - 250 V @Thickness 0.118 in |
UL |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 271 - 293 °C | 520 - 560 °F | |
| Middle Barrel Temperature | 282 - 304 °C | 540 - 580 °F | |
| Front Barrel Temperature | 293 - 316 °C | 560 - 600 °F | |
| Nozzle Temperature | 288 - 310 °C | 550 - 590 °F | |
| Melt Temperature | 293 - 316 °C | 560 - 600 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 48 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UL File Number | E178307 |
Users viewing this material also viewed the following:
- RheTech Products FT2400-648UV Thermoplastic Polyolefin, UV Stabilized, 848 Black
- Polykemi AB POLYfill PPC T10030 Polypropylene Copolymer, Mineral Reinforced
- Malvern Minerals Thermoplastic Polyester with Novakup® 1250 Silane-Treated Quartz Filler
- SABIC Innovative Plastics Ultem DT1800E PEI Blend (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP Stat-kon WX98547 PBT
- Sibur Nitrilast-26 Nitrile-Butadiene Rubber (NBR)
- A. Schulman POLYBATCH™ Treated Pine 60181U/4 Concentrate Based In LLDPE
- Polyram PlusTek RA301G8 Nylon 6.6 for Injection Molding, 40% Glass Fiber Reinforced, Heat Stabilized
- Covestro Texin® 990 Urethane Thermoplastic Elastomer
- Barlog Plastics KEBAFLEX SG 25 A.1 TPE-S, Shore A25, natural
Copyright © lookpolymers.com All Rights Reserved