LTL Color Compounds ColorFast® FRPBT220 PBT, Flame Retarded

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant
Manufacturer LTL Color Compounds
Trade Name ColorFast®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LTL Color Compounds ColorFast® FRPBT220 PBT, Flame Retarded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Super tough, flame retarded unreinforcedAll information provided by LTL Color Compounders, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ASTM D792
Linear Mold Shrinkage 0.022 cm/cm
0.022 in/in
0.125; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 124
124
ASTM D785
Tensile Strength, Yield 40.0 MPa
5800 psi
2.0 in/min; ASTM D638
Elongation at Break 145 %
145 %
2.0 in/min; ASTM D638
Flexural Strength 97.2 MPa
14100 psi
2.0 in/min; ASTM D790
Flexural Modulus 2.07 GPa
300 ksi
2.0 in/min; ASTM D790
Thermal Properties Metric English Comments
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Processing Properties Metric English Comments
Rear Barrel Temperature 232 - 249 °C
450 - 480 °F
Middle Barrel Temperature 238 - 254 °C
460 - 490 °F
Front Barrel Temperature 243 - 260 °C
470 - 500 °F
Nozzle Temperature 238 - 254 °C
460 - 490 °F
Melt Temperature 243 - 260 °C
470 - 500 °F
Mold Temperature 48.9 - 76.7 °C
120 - 170 °F
Drying Temperature 121 °C
250 °F
Dry Time 3 - 4 hour
3 - 4 hour
nominal; maximum drying time of 12 hours
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Shot Size 40 - 60 %
40 - 60 %
Vent Depth 0.00127 - 0.00254 cm
0.000500 - 0.00100 in
Screw Speed 40 - 70 rpm
40 - 70 rpm