NYCOA 27/300I Glass Filled Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | NYCOA, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NYCOA 27/300I Glass Filled Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass filled, flame retardant to UL 94 V-0 nylon 6Information provided by NYCOA, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ASTM D792 |
| Water Absorption | 0.95 % | 0.95 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 170 MPa | 24700 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 245 MPa | 35500 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.700 mm |
V-0 @Thickness 0.0276 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 225 °C | 437 °F | |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Front Barrel Temperature | 250 °C | 482 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 76.0 °C | 169 °F |
Users viewing this material also viewed the following:
- NOVA Chemicals EPS 33MB Modified Expandable Polystyrene
- Solvay Specialty Polymers Amodel® AE-4133 Polyphthalamide (PPA) (Unverified Data**)
- SABIC HP4023W Low Density Polyethylene for Blown Film
- Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes
- Lehmann & Voss LUVOCOM® 1105/MS/15/TF/15 PEEK, with PTFE, lubricant modified
- SABIC Innovative Plastics Valox® IQ8280SF PBT+PET
- Unitika E-RUNG60 Ultra high-rigidity PA6, Dry
- Compuestos Dominicanos Polycom C-550170 PVC
- 3M Cushion-Mount™ E1060 Plus Plate Mounting Tapes with Easy Mount Adhesive
- Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved