LTL Color Compounds ColorFast® FRPBT200 PBT, Flame Retarded
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRPBT200 PBT, Flame Retarded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
V-0 rated, unfilled PBTAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.015 - 0.023 cm/cm | 0.015 - 0.023 in/in | 0.125; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 58.6 MPa | 8500 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 80 % | 80 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 101 MPa | 14700 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C |
0.700 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 249 °C | 450 - 480 °F | |
| Middle Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Nozzle Temperature | 238 - 254 °C | 460 - 490 °F | |
| Melt Temperature | 243 - 260 °C | 470 - 500 °F | |
| Mold Temperature | 48.9 - 76.7 °C | 120 - 170 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 12 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00127 - 0.00254 cm | 0.000500 - 0.00100 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1112T PC Copolymer
- 3M Dyneon™ PVDF 1015/1001 Polyvinylidene Fluoride (discontinued **)
- Kingfa PBT-RG20 Flame Retardant, 20% Glass Fiber Reinforced PBT
- ITW Plexus Plexusâ„¢ MA330 Methacrylate Adhesive
- Borealis Himod™ FT5270 LDPE for Film
- Wellman Wellamid® GF1662-GY1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66/6
- Wellman Wellamid® GF1750-BK1 50% Glass Fiber Reinforced Nylon 6
- Clariant Renol PCSP0015 Polycarbonate, Carbon Fiber Filled
- BASF Capron® 8334G Impact Modified, 40% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- DuPont™ Sclairfilm® LWS-1 LMDPE Film, Laminating, 38.1 µm Thickness (discontinued **)