LTL Color Compounds ColorFast® FRA202 General Purpose ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRA202 General Purpose ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose V0/5VA-rated ABSAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | 0.125; ASTM D955 |
| Melt Flow | 11 g/10 min @Load 3.80 kg, Temperature 230 °C |
11 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 39.3 MPa | 5700 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 10 % | 10 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 57.9 MPa | 8400 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Temperature 22.8 °C |
4.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VA @Thickness 2.60 mm |
5VA @Thickness 0.102 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Wire Ignition, HWI | 7.0 - 15 sec @Thickness 1.50 mm |
7.0 - 15 sec @Thickness 0.0591 in |
UL746 |
| >= 120 sec @Thickness 3.00 mm |
>= 120 sec @Thickness 0.118 in |
UL746 | |
| High Amp Arc Ignition, HAI | >= 120 arcs @Time 1.50 sec |
>= 120 arcs @Time 0.000417 hour |
UL746 |
| >= 120 arcs @Time 3.00 sec |
>= 120 arcs @Time 0.000833 hour |
UL746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 182 °C | 340 - 360 °F | |
| Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Front Barrel Temperature | 210 - 221 °C | 410 - 430 °F | |
| Nozzle Temperature | 193 - 221 °C | 380 - 430 °F | |
| Melt Temperature | 193 - 232 °C | 380 - 450 °F | |
| Mold Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Drying Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 50 - 70 % | 50 - 70 % | |
| Vent Depth | 0.00381 - 0.00508 cm | 0.00150 - 0.00200 in | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UL File Number | E178307 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID: 8-15/3-5 nm Aligned Multi-Walled Carbon Nanotubes
- SABIC Innovative Plastics Cycoloy® CX7211 PC+ABS (Asia Pacific)
- PolyOne Edgetek® COC BLEND-15GF Natural Cyclic Olefin Copolymer (COC)
- Techmer ES HiFill® PA6 GF/M40 HS L BK 40% Glass/Mineral Filled
- Teknor Apex APEX® 3302-80 Polyvinyl Chloride, Flexible
- Lubrizol Estane® S168D Thermoplastic Polyurethane
- Diamond Polymers ABS VP-11 ELG
- DuPont Performance Polymers Zytel® 70G33HS1L NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved