Material Notes:

Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Physical Properties	Metric	English	Comments
Specific Gravity	1.32 g/cc	1.32 g/cc	Method A; ASTM D792
Water Absorption	0.10 %	0.10 %	at 24 hrs; ASTM D570
Linear Mold Shrinkage	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0070 - 0.0080 cm/cm	0.0070 - 0.0080 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	182 MPa	26400 psi	ASTM D638
Tensile Strength, Yield	182 MPa	26400 psi	ASTM D638
Elongation at Break	3.7 %	3.7 %	ASTM D638
Elongation at Yield	3.7 %	3.7 %	ASTM D638
Tensile Modulus	9.58 GPa	1390 ksi	ASTM D638
Flexural Strength	290 MPa	42100 psi	ASTM D790
Flexural Modulus	9.31 GPa	1350 ksi	ASTM D790
Izod Impact, Notched	1.39 J/cm @Thickness 3.18 mm	2.60 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	12.4 J/cm @Thickness 3.18 mm	23.2 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Notched (ISO)	14.1 kJ/m²	6.71 ft-lb/in²	ISO 180
Izod Impact, Unnotched (ISO)	78.3 kJ/m²	37.3 ft-lb/in²	ISO 180
Falling Dart Impact	14.0 J	10.3 ft-lb	ASTM D3763
Impact Test	3.04 J	2.24 ft-lb	Multi-Axial Instrumented Impact Energy; ISO 6603-2

Thermal Properties	Metric	English	Comments
CTE, linear	40.0 µm/m-°C @Temperature 20.0 °C	22.2 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	72.0 µm/m-°C @Temperature 20.0 °C	40.0 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
Deflection Temperature at 0.46 MPa (66 psi)	214 °C	417 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	198 °C	388 °F	Unannealed; ASTM D648
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Processing Properties	Metric	English
Melt Temperature	268 - 274 °C	514 - 525 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	4 hour	4 hour
Back Pressure	0.172 - 0.345 MPa	24.9 - 50.0 psi