DuPont Performance Polymers Zytel® FE3734 NC010 Nylon 612 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® FE3734 NC010 Nylon 612
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced Polyamide 612 Zytel FE3734 NC010 is an unreinforced lubricated polyamide 612 resin suitable for injection molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | DAM; ISO 1183 |
| Water Absorption | 3.0 % @Thickness 2.00 mm |
3.0 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Moisture Absorption | 1.30 % @Thickness 2.00 mm |
1.30 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Viscosity Test | 95 cm³/g | 95 cm³/g | DAM; ISO 307 1157 1628 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 |
| 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
DAM | |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | DAM; ISO 294-4 2577 |
| 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
DAM; ASTM D149 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | DAM; ISO 2039-2 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50%RH; ISO 527-1/-2 |
| 59.0 MPa | 8560 psi | DAM; ISO 527-1/-2 | |
| Elongation at Break | 30 % | 30 % | 50%RH; Nominal; ISO 527-1/-2 |
| 38 % | 38 % | DAM; Nominal; ISO 527-1/-2 | |
| Elongation at Yield | 13 % | 13 % | DAM; ISO 527-1/-2 |
| 21 % | 21 % | 50%RH; ISO 527-1/-2 | |
| Tensile Modulus | 1.60 GPa | 232 ksi | 50%RH; ISO 527-1/-2 |
| 2.40 GPa | 348 ksi | DAM; ISO 527-1/-2 | |
| Flexural Modulus | 2.20 GPa | 319 ksi | DAM; ISO 178 |
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 0.480 J/cm² | 2.28 ft-lb/in² | DAM; ISO 179/1eA |
| 0.530 J/cm² | 2.52 ft-lb/in² | 50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | DAM; ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Lubricants | |
| Release agent | ||
| Delivery Form | Pellets | |
| Part Marking Code | >PA612< | ISO 11469 |
| Processing | Injection Moulding | |
| Regional Availability | Asia Pacific | |
| Europe | ||
| Global | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Resin Identification | PA612 | |
| PA612 | ISO 1043 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTech™ HDPE GRC20 Glass Reinforced
- Polykemi AB POLYabs F00L ABS
- I. Stern BLK100 High Impact Polystyrene Extrusion Grade
- Indium Corp. Indalloy 95 Bismuth-Lead-Tin Solder Alloy
- LG Chemical TR-558 Transparent ABS, Humidity Resistance, Natural and Colored Pellets
- Lucent Polymers GPP-240 Homopolymer Polypropylene, 40% Glass Fiber Reinforced, Chemically Coupled
- SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP (Europe-Africa-Middle East)
- Tipco Tipcolite® TMS 111 Phenolic Compound, Cellulose Pulp, in fluffy form, having Soft Flow & High Strength
- ERG Aerospace Reticulated Vitreous Carbon (RVC)
- 3M Scotch-Weld™ 3750 Tan Hot Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved