Samsung Cheil Industries Infino® SC-1220R PC, Unreinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® SC-1220R PC, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 22 g/10 min @Load 1.20 kg, Temperature 300 °C |
22 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 62.8 MPa | 9100 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 90 % | 90 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 92.2 MPa | 13400 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 5.88 J/cm @Thickness 3.17 mm |
11.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 144 °C | 291 °F | B/50; ISO R306 |
| Flammability, UL94 | V-2 @Thickness 0.800 - 3.20 mm |
V-2 @Thickness 0.0315 - 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 0.80 % @Thickness 3.20 mm |
<= 0.80 % @Thickness 0.126 in |
ASTM D1003 |
| Transmission, Visible | 89 % @Thickness 3.20 mm |
89 % @Thickness 0.126 in |
ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 110 sec | 110 sec | Tungsten; ASTM D495 |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IE7020 Unitape Unidirectional Polyethylene-Glass Composite
- Polykemi AB POLYabs N30 ABS
- PolyMirae Moplen EP540S Injection Molding Grade Polypropylene
- PolyOne Geon™ Vinyl Flexible XV3796 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Nilit FRIANYL A63 KG20 Nylon 6.6 for injection molding, 20% chalk filled
- IDI Composites M-207 Thermoset Polyester, Sheet
- Tisan TISAKRIL® Flame Retardant (V0) ABS
- A. Schulman FORMION™ FI 226 40% Glass Fiber Reinforced Ionomer / Nylon Alloy
- Ecomass® 4450CI86 Carbonyl Iron Filled Polypropylene
- Arlon 23234R025 0.025" (0.635 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved