LG Chemical LUPOY SC5004T PC/Polyester, Transparency
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY SC5004T PC/Polyester, Transparency.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/Polyester, General Purpose, Transparency, High FlowApplication: Keypad for Mobile PhoneCAS: 103598-77-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 30 g/10 min @Load 1.20 kg, Temperature 300 °C |
30 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 60.8 MPa @Thickness 3.20 mm |
8820 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 150 % @Thickness 3.20 mm |
>= 150 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 97.1 MPa @Thickness 3.20 mm |
14100 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 3.20 mm |
327 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 6.86 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 12.9 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 265 - 280 °C | 509 - 536 °F | Injection Molding |
| Front Barrel Temperature | 265 - 280 °C | 509 - 536 °F | Injection Molding |
| Nozzle Temperature | 265 - 295 °C | 509 - 563 °F | Injection Molding |
| Melt Temperature | 265 - 290 °C | 509 - 554 °F | Injection Molding |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Injection Molding |
| Drying Temperature | 95.0 - 105 °C | 203 - 221 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs NI650 {Ni(NH3)6}I2 Hexaminenickel(II) iodide
- Menzolit Menzolit® SMC 1650 Unsaturated Polyester UP
- SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific)
- SABIC Innovative Plastics NORYL GTX GTX918WR PPE+PS+PA
- Tipco Tipcolite® THD 411 Phenolic Compound, Mica, Asbestos & Cellulose, Medium Flow & High Electrical Properties
- Tra-Con Tra-Bond 2119 Low Viscosity Glass Laminating Adhesive
- 3M Scotch-Weld™ 183 B/A Tan Epoxy Adhesive
- A. Schulman ComAlloy E-16822-1B Internally Lubricated, Carbon Fiber Reinforced Nylon 6/6
- Bhansali Engineering Abstron HI-40 B ABS High Impact Injection Molding
- Polyram RamSter PF201 PBT, General Purpose, Medium Viscosity
Copyright © lookpolymers.com All Rights Reserved