LG Chemical LUPOY GP5006B PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP5006B PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, General Purpose, High FlowApplication: Miscellaneous GoodsCAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 55.9 MPa @Thickness 3.20 mm |
8110 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 100 % @Thickness 3.20 mm |
>= 100 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 90.2 MPa @Thickness 3.20 mm |
13100 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 3.20 mm |
327 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 2.94 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
>= 5.51 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| >= 5.69 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 10.7 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C @Thickness 6.40 mm |
237 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Front Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Nozzle Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N330 (HAF) Filler
- Gwent Electronic Materials G2020520D1 Gold Metallo-Organic Ink
- H.C. Starck Amperit® 518.088 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- KaMin Polyfil® 80 Kaolin Clay - Calcined
- 3M 7218SA Screen Printable Polyester Performance Label Products with Structured Adhesive
- 3M Scotchcal™ 1000-25 Graphic Film
- PolyOne Synprene® RT-3890MS Thermoplastic Elastomer - SBC (discontinued **)
- Solvay Specialty Polymers Veradel® 3320GF Polyethersulfone (PESU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved