LG Chemical LUPOY GP-1000 General Purpose Modified PC, Unreinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP-1000 General Purpose Modified PC, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive front ends, cluster pad main panel (instrument panel), lower cluster pad main, console box, glove box cover, door, wheel cover and cap, defroster grill, back mirror housingElectrical and Electronic: Monitor housing, fax housing, notebook PC housing, cellular phone case, fax and copy machine frame, CD ROM drive tray and main frame, relay case, connector, switchIndustrial Parts and Household Appliance: Helmet, terminal box, electrical tool housing, industrial bobbin, distributing board box, power tool component, gears and cams, water meter housingInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.155 GPa | 312.6 ksi | ASTM D790 |
| Izod Impact, Notched | 7.85 J/cm @Temperature 23.0 °C |
14.7 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 255 - 270 °C | 491 - 518 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |
| Nozzle Temperature | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Plaskolite Optix® CP - 41 HF General Purpose Acrylic Resin
- Oxford Polymers 15GF-V0 15% Glass Fiber Reinforced Polybutylene Terephthalate (PBT), Flame Resistant
- SABIC Innovative Plastics Cycoloy® FXC810AR PC+ABS
- PolyOne Geon™ Vinyl Dry Blend E1354 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Microtherm Group Marineguard® Filament Reinforced Silica Marine Insulation Panel, Flexible and Waterproof
- Sharadaa Ceramics ZAP 001 Smart Cast Application
- Samyang Trirex® 3025R Polycarbonate with Heat Stabilizer
- Arlon Ultrapad™ 55072R125D 0.125" (3.17 mm) Cured Silicone Rubber with Fiberglass Substrate
- Akzo Nobel Expancel® 054 WU 40 Wet unexpanded microspheres
Copyright © lookpolymers.com All Rights Reserved