SABIC Innovative Plastics LNP Stat-kon PE002 PA 6 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-kon PE002 PA 6 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* PE002 is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D 792
1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.0 %

@Time 86400 sec
1.0 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D 955
0.0041 cm/cm

@Time 86400 sec
0.0041 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D 955
0.0074 cm/cm

@Time 86400 sec
0.0074 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16500 psi
ASTM D 638
115 MPa
16700 psi
Type I, 5 mm/min; ASTM D 638
124 MPa
18000 psi
ISO 527
124 MPa
18000 psi
5 mm/min; ISO 527
Elongation at Break 6.8 %
6.8 %
ASTM D 638
6.8 %
6.8 %
Type I, 5 mm/min; ASTM D 638
8.0 %
8.0 %
ISO 527
8.1 %
8.1 %
5 mm/min; ISO 527
Tensile Modulus 8.67 GPa
1260 ksi
1 mm/min; ISO 527
11.72 GPa
1700 ksi
50 mm/min; ASTM D 638
Flexural Strength 172 MPa
24900 psi
ASTM D 790
179 MPa
26000 psi
1.3 mm/min, 50 mm span; ASTM D 790
185 MPa
26800 psi
ISO 178
Flexural Yield Strength 185 MPa
26800 psi
2 mm/min; ISO 178
Flexural Modulus 5.51 GPa
799 ksi
ASTM D 790
5.52 GPa
801 ksi
1.3 mm/min, 50 mm span; ASTM D 790
7.40 GPa
1070 ksi
ISO 178
7.40 GPa
1070 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.640 J/cm

@Temperature 23.0 °C
1.20 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 1.22 J/cm

@Temperature 23.0 °C
2.29 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 8.00 kJ/m²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
81.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 39.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
21.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
39.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
21.7 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
39.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
22.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
219 °C

@Thickness 3.20 mm
426 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 197 °C
387 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
197 °C

@Thickness 3.20 mm
387 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D 257