LG Chemical LUPOY GN5151RF PC/ABS Mineral Filler
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | LG Chemical LUPOY GN5151RF PC/ABS Mineral Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame RetardantApplication: E&E (Housing), IT/OA (Notebook PC Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.040 | 0.040 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm <br>@Thickness 3.20 mm |
0.0020 - 0.0040 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C |
9.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.8 MPa <br>@Thickness 3.20 mm |
8820 psi <br>@Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 15 % <br>@Thickness 3.20 mm |
15 % <br>@Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 108 MPa <br>@Thickness 3.20 mm |
15600 psi <br>@Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 4.12 GPa <br>@Thickness 3.20 mm |
597 ksi <br>@Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C |
1.84 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C <br>@Thickness 6.40 mm |
203 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C <br>@Thickness 1.00 - 1.10 mm |
140 °F <br>@Thickness 0.0394 - 0.0433 in |
|
| UL RTI, Mechanical with Impact | 60.0 °C <br>@Thickness 1.00 - 1.10 mm |
140 °F <br>@Thickness 0.0394 - 0.0433 in |
|
| UL RTI, Mechanical without Impact | 60.0 °C <br>@Thickness 1.00 - 1.10 mm |
140 °F <br>@Thickness 0.0394 - 0.0433 in |
|
| Flammability, UL94 | V-0 <br>@Thickness 1.00 - 1.10 mm |
V-0 <br>@Thickness 0.0394 - 0.0433 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 245 - 265 °C | 473 - 509 °F | Injection Molding |
| Front Barrel Temperature | 260 - 275 °C | 500 - 527 °F | Injection Molding |
| Nozzle Temperature | 260 - 275 °C | 500 - 527 °F | Injection Molding |
| Melt Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.981 - 1.96 MPa | 142 - 284 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ V 3085A-S0098 Thermoplastic Elastomer (TPE)
- Polikim ULPOLEN® 500 UHMWPE Standard
- Iran Petrochemical (PCC) S 30 G Polypropylene
- SABIC Innovative Plastics LNP LUBRICOMP RFL36SXC PA 66 (Europe-Africa-Middle East)
- Saint-Gobain CHR® T Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Borealis BorSafe™ HE3490-LS-H HDPE Compound for Pressure Pipes
- Covestro Bayblend® W85 XF* Polycarbonate + ASA
- Fainplast Compounds HG 80/2 Flexible PVC, Sheathing for High Temperatures
- Azoty Tarnow™ TARFLEN SM-S15G2 PTFE
Copyright © lookpolymers.com All Rights Reserved