HP Alloys Alloy X, 5% Cold Worked

Category	Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer	High Performance Alloys, Inc
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	HP Alloys Alloy X, 5% Cold Worked.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

5% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, and Haynes International.

Physical Properties	Metric	English	Comments
Density	8.22 g/cc	0.297 lb/in³

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	848 MPa	123000 psi
Tensile Strength, Yield	565 MPa	81900 psi
Elongation at Break	32 %	32 %
Modulus of Elasticity	205 GPa	29700 ksi

Thermal Properties	Metric	English
CTE, linear	15.0 µm/m-°C @Temperature 20.0 - 500 °C	8.33 µin/in-°F @Temperature 68.0 - 932 °F
	16.6 µm/m-°C @Temperature 20.0 - 1000 °C	9.22 µin/in-°F @Temperature 68.0 - 1830 °F
Thermal Conductivity	16.9 W/m-K @Temperature 400 °C	117 BTU-in/hr-ft²-°F @Temperature 752 °F
Melting Point	1260 - 1355 °C	2300 - 2471 °F
Solidus	1260 °C	2300 °F
Liquidus	1355 °C	2471 °F

Component Elements Properties	Metric	English
Boron, B	<= 0.0080 %	<= 0.0080 %
Carbon, C	0.10 %	0.10 %
Chromium, Cr	22 %	22 %
Cobalt, Co	1.5 %	1.5 %
Iron, Fe	18 %	18 %
Manganese, Mn	<= 1.0 %	<= 1.0 %
Molybdenum, Mo	9.0 %	9.0 %
Nickel, Ni	47 %	47 %
Silicon, Si	<= 1.0 %	<= 1.0 %
Tungsten, W	0.60 %	0.60 %